Tuning the Interfacial Chemistry for Stable and High Energy Density Aqueous Sodium-Ion/Sulfur Batteries
Mukesh Kumar,Tharamani C. Nagaiah
DOI: https://doi.org/10.1149/ma2023-024612mtgabs
2023-12-22
ECS Meeting Abstracts
Abstract:The environmental-related issues arising from the fossil fuel assorted industrial revolution and worldwide development have prompted the quest for rechargeable batteries. In these predicaments, lithium-ion batteries (LIBs) took ownership to reshape our lives. However, the limited abundance, non-uniform geographical distribution and severe flammability of organic electrolytes, increase the uncertainty over their large-scale application. Recently, aqueous rechargeable sodium-ion batteries (ARSIBs) have gained considerable curiosity for large-scale energy storage due to their much-assured safety, environment friendliness, high-rate capacity, and low cost. However, the prospects of ARSIBs seeing commercial success remained remote due to the narrow water stability window (1.23 V), which translates into low cell voltage (< 1.6 V), low energy density (< 70 Wh Kg -1 ), and compromised cycling stability. The aforesaid dilemmas can be resolved by generating a protective layer known as a solid electrolyte interface (SEI) like in organic electrolytes. However, the SEI concept in aqueous electrolytes is relatively unexplored, as water dissociation leads to O 2 and H 2 , and will enhance the parasitic reactions. The SEI formed in WiSE due to salt reduction is often inhomogeneous with a porous mosaic structure and is susceptible to mechanical cracking, and increase the overall cost. Hence, high-capacity electrodes and high voltage electrolytes capable of forming a stable SEI are urgently required to fulfill the dream of the large-scale application of ARSIBs. Recently low cost, highly abundant sulfur-based electrode material has attracted significant research attention due to its high theoretical capacity (1675 mA h g -1 ) and energy density. However, sluggish sulfur redox kinetics, acute polysulfide shutting, dendritic growth on the metal-based anode and low conductivity of sulfur and its discharge products proves to be a major roadblock for its commercialization. Utilizing abundant sulfur in an aqueous electrolyte along with abundant Na + can resolve the kinetics and conductivity anxieties and leads to a new greener and safer Na-ion/S batteries chemistry. However lower order polysulfide dissolution in water is more feasible, leading to the rapid capacity decay and active sulfur loss due to H 2 S formation. Polysulfide dissolution is an interfacial mechanism occurring at the electrode-electrolyte interface and depends on both electrode and electrolyte merits. Therefore, an effective approach will be to couple efficient sulfur host with an electrolyte capable of generating a stable SEI on the electrode surface to prevent the direct attack of water on polysulfide. Herein we have explored urchin-like CoWO 4 as a sulfur host coupled with Na-W-U-D electrolyte. The CoWO 4 exhibits high conductivity, strong chemical interaction for sulfur and its discharge products, and urchin-like morphology having exposed edges facilitate the charge transport results in excellent polysulfide redox kinetics. The high voltage Na-W-U-D electrolyte was prepared by mixing NaClO 4 , urea, and N, N-dimethylformamide DMF in 1:2:1 ratio in water. Each component in the electrolyte plays an important role. Urea has very high water solubility and tends to form stable SEI, while DMF has a high dielectric constant, good solvation ability, and develop stabilize SEI. As a result, Na-W-U-D shows a stability window close to the 3.1 V regime due to reduced water activity resulting from complex ion solvent interaction and stable and uniform SEI formation, consisting of Na 2 CO 3 , polyurea, and reduction products of DMF. Despite the addition of DMF, non-flammable features of aqueous electrolytes remain well maintained. Herein for the first time, the SEI concept was successfully used for the aq. Na-ion/S battery. We discovered that the lower water activity of Na-W-U-D electrolyte hindered polysulfide dissolution and stable SEI prevent the direct attack of water on polysulfide and results in extended cycling stability. At the same time, the urchin-like CoWO 4 host enhances the sluggish polysulfide redox kinetics and provides an abundant anchoring site for polysulfide adsorption. We investigate the effect of time, C-rate, depth of discharge, and dissolved oxygen on polysulfide dissolution and self-discharge of the negative electrode. The high electrode capacity combined with the safety and stable SEI of Na-W-U-D electrolyte translated into a record high initial capacity of 834 mA h g -1 w.r.t sulfur, with remarkable cycling stability up to 500 cycles @ 0.5 C. Post analysis by SEM and XPS, evident that the stable SEI consists of Na 2 CO 3 , polyurea, and reduced products of DMF (CO and NHMe 2 ), which also prevent the negative electrode from self-discharge by mitigating the parasitic reaction of dissolved oxygen in the electrolyte. Moreover, a full cell assembled by integrating S@CoWO 4 anode and Na 0.44 MnO 2 cathode showed remarkable stability and a high energy density of 119 Wh kg -1 , making it a promising candidate for a future energy storage system. Figure 1