Flexible 3D Porous MoS 2 /CNTs Architectures with ZT of 0.17 at Room Temperature for Wearable Thermoelectric Applications
Jiahui Li,Qiuwei Shi,Jason A Röhr,Hao Wu,Bo Wu,Yang Guo,Qinghong Zhang,Chengyi Hou,Yaogang Li,Hongzhi Wang
DOI: https://doi.org/10.1002/adfm.202002508
IF: 19
2020-07-12
Advanced Functional Materials
Abstract:<p>Developing materials that possess high electrical conductivities (σ) and Seebeck coefficients (<i>S </i>), low thermal conductivities (κ), and excellent mechanical properties is important to realize practical thermoelectric (TE) devices. Here, 3D hierarchical architectures consisting of hybrid molybdenum disulfide (MoS<sub>2</sub>)/carbon nanotubes (CNTs) films are fabricated with the goal of increasing σ and decreasing κ. In these films, perpendicularly orientated CNTs interpenetrate restacked MoS<sub>2</sub> layers to form a 3D architecture, which increases the specific surface area and charge concentration. The MoS<sub>2</sub>/20 wt% CNTs film shows high σ (235 ± 5 S∙cm<sup>−1</sup>), high <i>S </i> (68 ± 2 µV∙K<sup>−1</sup>), and low κ (19 ± 2 mW∙m<sup>−1</sup>∙K<sup>−1</sup>). The corresponding figure of merit (<i>ZT </i>) reaches 0.17 at room temperature, which is 65 times higher than that of pure MoS<sub>2</sub> film. In addition, the MoS<sub>2</sub>/20 wt% CNTs film shows a tensile stress of 38.9 MPa, which is an order of magnitude higher than that of a control MoS<sub>2</sub> film. Using the MoS<sub>2</sub>/CNTs film as an active material and human body as a heat source, a flexible, wearable TE wristband is fabricated by weaving seven strips of the 3D porous MoS<sub>2</sub>/CNTs film. The wristband achieves an output voltage of 2.9 mV and corresponding power output of 0.22 µW at a temperature gradient of about 5 K.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology