Holocellulose Nanofibril-Assisted Intercalation and Stabilization of Ti 3 C 2 T x MXene Inks for Multifunctional Sensing and EMI Shielding Applications
Yian Chen,Yuehu Li,Yu Liu,Pan Chen,Cunzhi Zhang,Haisong Qi
DOI: https://doi.org/10.1021/acsami.1c10583
2021-07-21
Abstract:2D transition-metal carbide/nitride (MXene)-based conductive inks have received tremendous attention due to their high electrical conductivity and other fascinating properties. However, the unstability of MXene-based inks, low fabrication yield of MXene flakes, and poor mechanical properties of printed products strongly limit the proper and large-scale printing of MXene patterns. Here, functioning as a dispersant, an intercalation agent, and reinforcement, sulfated holocellulose nanofibrils (HCNFs) with a unique "core–shell" structure are conducive to the fabrication, storage, and subsequent printing of MXene inks. The MXene/HCNF (MH) ink with high yield (97.2%), good stability, and good homogeneity exhibits excellent printing performance (high resolution and good coverage). It could print various products with adjustable thicknesses and electrical conductivity properties on different substrates. The products printed by the MH ink can be applied as multifunctional sensing materials responding to multiple external stimuli, such as stress/strain, blowing, humidity, and temperature. Furthermore, the resulting products also display a high electromagnetic interference (EMI) shielding effectiveness (SE) of 54.3 dB at a shallow thickness of 100 μm and an excellent specific EMI SE of SSE/<i>t</i> of 7159 dB cm<sup>2</sup> g<sup>–1</sup>.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c10583?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c10583</a>.Diameter distribution and length distribution of HCNF; FTIR and XRD spectra of HCNF and pine powder; mass fractions of elements C, N, H, and S and DS in HCNF and CNF with different reaction times; zeta potential results of HCNF, CNF, and MH55 ink with different DS values; SEM images of Ti<sub>3</sub>AlC<sub>2</sub>, multilayered Ti<sub>3</sub>C<sub>2</sub>T<i><sub>x</sub></i>, and MXene; AFM image of Ti<sub>3</sub>C<sub>2</sub>T<i><sub>x</sub></i>; XPS spectra of Ti<sub>3</sub>AlC<sub>2</sub> and MXene; FTIR and XRD spectra of HCNF, Ti<sub>3</sub>AlC<sub>2</sub>, MH91, MH82, and MH64; stability of the MXene/HCNF ink; comparison of zeta potential and rheological values of MXene/HCNF, MXene/CNF, and MXene ink; ink formula, ink concentration, and viscosity for different printing processes; photograph showing the LED light connected by the conductive traces printed on the paper substrate with the MH ink; electrical conductivity changes of oriented products on paper; electrical conductivity changes of oriented products with different MH inks; and schematic illustration of MXene network evolution for tensile sensing, humidity sensing, and temperature sensing processes (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c10583/suppl_file/am1c10583_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology