Abstract:Experimental adhesives containing co-doped metaloxide nanoparticles were demonstrated to display strong and long-term antibacterial properties against Streptococcus mutans biofilms. The present study represents an effort to characterize the shear-bond strength (SBS) and color stability (CS) of these novel biomaterials. Experimental adhesives were obtained by dispersing nitrogen and fluorine co-doped titanium dioxide nanoparticles (NF_TiO2, 10%, 20% or 30%, v/v%) into OptiBond Solo Plus (OPTB). Dentin surfaces were wet-polished (600-Grit). Specimens (n = 5/group) of Tetric EvoCeram were fabricated and bonded using either OPTB or experimental (OPTB + NF_TiO2) adhesives. Specimens were stored in water (37 °C) for twenty-four hours (T1), three months (T2), and six months (T3). At T1, T2, or T3, specimens were removed from water storage and were tested for SBS. Disc-shaped specimens (n = 10/group; d = 6.0 mm, t = 0.5 mm) of adhesives investigated were fabricated and subjected to thermocycling (10,000 cycles, 5−55 °C, 15 s dwell time). Specimens’ colors were determined with a VITA Easyshade® V spectrophotometer (after every 1000 cycles). SBS data was analyzed using two-way ANOVA and post-hoc Tukey tests, while CS data was analyzed using one-way ANOVA and post-hoc Tukey tests (α = 0.05). Mean values of SBS ranged from 16.39 ± 4.20 MPa (OPTB + 30%NF_TiO2) to 19.11 ± 1.11 MPa (OPTB), from 12.99 ± 2.53 MPa (OPTB + 30% NF_TiO2) to 14.87 ± 2.02 (OPTB) and from 11.37 ± 1.89 (OPTB + 20% NF_TiO2) to 14.19 ± 2.24 (OPTB) after twenty-four hours, three months, and six months of water storage, respectively. Experimental materials had SBS values that were comparable (p > 0.05) to those from OPTB independently of nanoparticle concentration or time-point considered. Experimental materials with higher NF_TiO2 concentrations had less intense color variations and were more color stable than OPTB even after 10,000 thermocycles. In combination, the results reported have demonstrated that experimental adhesives can establish strong and durable bonds to human dentin while displaying colors that are more stable, thereby suggesting that the antibacterial nanotechnology investigated can withstand the harsh conditions within the oral cavity without compromising the esthetic component of dental restorations.

Laboratory evaluation and clinical application of a new one-bottle adhesive

Reconstruction of a Demineralized Dentin Matrix Via Rapid Deposition of CaF2 Nanoparticles in Situ Promotes Dentin Bonding.

Influence of collagen cross-linkers addition in phosphoric acid on dentin biomodification and bonding of an etch-and-rinse adhesive

Evaluating the advancements in a recently introduced universal adhesive compared to its predecessor

Bond strength test of two resin adhesives to fiber post and the characteristics of adhesive interface between dentine and fiber post under confocal laser scanning microscopy

Cross-compatibility of methacrylate-based resin composites and etch-and-rinse one-bottle adhesives

Longitudinal bond strength of a universal adhesive and chemical dentin characterization under different acid etching protocols

Correlation between bond strength and nanomechanical properties of adhesive interface

Evaluation of Bond Durability, Surface Morphology, and Remineralization at the Adhesive Interface with Dentin Bonding Agents Modified with Silica-doped Nanohydroxyapatite

Adhesive Interfacial Characteristics and the Related Bonding Performance of Four Self-Etching Adhesives with Different Functional Monomers Applied to Dentin.

Nanoscopic dynamic mechanical analysis of resin-infiltrated dentine, under in vitro chewing and bruxism events

The Molecular and Mechanical Characteristics of Biomimetic Composite Dental Materials Composed of Nanocrystalline Hydroxyapatite and Light-Cured Adhesive

Effect of a Novel Quaternary Ammonium Methacrylate Polymer (QAMP) on Adhesion and Antibacterial Properties of Dental Adhesives

Experimental study of bonding strength between resin composite direct core build-up materials and dentin in vitro

An investigation of the shear bond strength of compomer restorative material to enamel and dentine

A Confocal Optical Microscope Study of the Morphology of the Tooth/Restoration Interface using Scotchbond 2 Dentin Adhesive

Influence of cavity disinfectant and adhesive systems on the bonding procedure in demineralized dentin - a one-year in vitro evaluation

A Research on Bond Strength and Interface of Dentin Adhesives

Nanoindentation Mapping and Bond Strength Study of Adhesive–Dentin Interfaces

Shear Bond Strength and Color Stability of Novel Antibacterial Nanofilled Dental Adhesive Resins

Adhesive performance of a multi-mode adhesive system: 1-Year in vitro study