Superior dielectric energy storage performance of ultrafine-grained BNT-SBT solid-solution ceramics by solution combustion synthesis

Qiyu Long,Chengyang Zuo,Shihong Xiao,Fu Du,Lei Chen,Xianhua Wei

DOI: https://doi.org/10.1016/j.ceramint.2024.07.062

IF: 5.532

2024-08-10

Ceramics International

Abstract:The micrometer scale grain size and large remnant polarization of Bi 0.5 Na 0.5 TiO 3 (BNT) ferroelectric ceramics severely constrain the breakdown strength and energy efficiency, respectively, restricting their energy storage application despite their large polarization. Hereby, superior energy storage performance is reported by a synergistic strategy of introducing Sr 0.7 Bi 0.2 TiO 3 (SBT) relaxor ferroelectrics and a solution combustion synthesis (SCS) method. The BNT-SBT solid-solution ceramics are comparatively investigated by the two methods, conventional sintering (CS) and SCS. An ultrafine average grain size of ∼0.39 μm was obtained in the SCS-derived ceramic, and thus exhibits an ultra-high critical electric field of 548 kV/cm, and a high recoverable energy density of ∼5.69 J/cm 3 . Those key energy storage parameters are superior to those of the previous reported samples prepared by the CS method. Meanwhile, a high energy efficiency ∼90 %, a large power density of ∼130.44 MW/cm 3 (at 320 kV/cm), and an ultrafast discharge time of ∼61.7 ns are also achieved. This study indicates that grain engineering combing with chemical design is an effective way to enhance the dielectric energy storage performance.

materials science, ceramics