Abstract:In the present study, low-cost, environmentally friendly, single-step, high productive novel Iron-oxide nanoparticles (NPs) were prepared from scrap iron using a green synthesis method to remove Pb (II) from aqueous solution. The characterization of synthesized nanoparticles was conducted by UV-vis spectroscopy. The crystalline structure and the phase change were clarified by XRD. FE-SEM was done to know the morphology of iron oxide nanoparticles, and the average surface area of 46.856 m2/g was found by the BET surface area analyzer. The XRD plot shows that the obtained magnetite Fe3O4 combines FeO and Fe2O3 as the synthesis was conducted in the open atmosphere. The SEM images confirm the formation of iron oxide nanoparticles with a size of 31 nm. The removal efficiency of the adsorbent was carried out by optimizing the different operational parameters like pH, time, adsorbent dosage, initial concentration of metal ion, contact time by batch studies. The obtained pHzpc (pH 5.7) value indicates that the adsorption process will be favorable at higher pH. The maximum removal efficiency and uptake capacity of lead were 98% and 68.07 mg/g, respectively. Adsorption data obtained were analyzed with Langmuir and Freundlich isotherm equations. The equilibrium data are fitted by Langmuir isotherm in a superior way than that of Freundlich isotherm. The results show that homogeneous adsorption of the metal ion favors heterogeneous adsorption. The maximum adsorption capacity of iron oxide NPs was calculated through Langmuir isotherm was Qmax (68.07) mg/g. Moreover, the adsorption of metal ions with time was also analyzed with the pseudo 1st and pseudo 2nd kinetic equations. The kinetic data are fitted more in the pseudo 2nd order reaction. Adsorption capacity calculated through pseudo 2nd order equation was qe (51.81) mg/g. This literature verifies that NPs synthesized from scrap iron as precursors prove to be an attractive option for removing heavy metals.

Green Synthesis of Iron (II, III)-polyphenol Nanoparticles and Their Adsorption of Malachite Green

Green synthesis of iron nanoparticle by tea extract (polyphenols) and its selective removal of cationic dyes

Green synthesis of iron nanoparticles using mulberry leaf extract: characterization, identification of active biomolecules, and catalytic activity

Green sulfidated iron oxide nanocomposites for efficient removal of Malachite Green and Rhodamine B from aqueous solution

GREEN SYNTHESIS OF IRON-OXIDE NANOPARTICLES USING SCRAP IRON AS PRECURSOR FOR THE REMOVAL OF PB (II) FROM AQUEOUS MEDIUM

Green Synthesis Of Bimetallic Iron/Copper Nanoparticles Using Ficus Leaves Extract For Removing Orange G(OG) Dye From Aqueous Medium

Effective Adsorption of Malachite Green with Silica Gel Supported Iron-Zinc Bimetallic Nanoparticles

Synthesis of superparamagnetic Fe3O4 nanoparticles coated with green tea polyphenols and their use for removal of dye pollutant from aqueous solution

Green Synthesis of Iron Nanoparticles Using Green Tea and Its Removal of Hexavalent Chromium

Enhanced adsorption of malachite green onto a composite material activated carbon and iron(III) oxide nanoparticles: isotherm, kinetic, and thermodynamic study

Engineered hybrid iron‐cobalt metal oxide nanoparticles for effective adsorption of malachite green dye

A Green Synthesis of Iron/Copper Nanoparticles as a Catalytic of Fenton-like Reactions for Removal of Orange G Dye

Green Synthesis of Iron Nanoparticles Using Plumeria and Jatropha: Characterization and Investigation of Their Adsorption, Regeneration and Catalytic Degradation Efficiencies

Green Synthesis, Characterization and Application of Proanthocyanidins-Functionalized Fe3O4 Magnetic Nanocomposites

Green Synthesis of Iron Oxide Nanoparticles and Their Modification with CTAB for the Decolorization of Dye Reactive Blue 238

Green Synthesis, Characterization and Application of Proanthocyanidins-Functionalized Fe<sub>3</sub>O<sub>4</sub> Magnetic Nanocomposites

Fabrication and Characterization Fe3O4/Humic Acid for the Efficient Removal of Malachite Green

Green Synthesis of Iron Nanoparticles-Modified Biochar For Efficient Adsorption of Cd(II) From Aqueous Solution

Greener and size-specific synthesis of stable Fe-Cu oxides as earth-abundant adsorbents for malachite green

Green Synthesis of Iron Oxide Nanoparticles Using Psidium guajava L. Leaves Extract for Degradation of Organic Dyes and Anti-microbial Applications

Green Synthesis, Characterization and Application on the Proanthocyanidins-Functionalized Fe3O4 @ Ag Nanoparticles