Synthesized high performance UV-cured wood wax oil using Irgacure 2959 modified thistle oil and linseed oil

Yijuan Chang,Zhihui Wu

DOI: https://doi.org/10.1016/j.indcrop.2024.118952

IF: 6.449

2024-06-17

Industrial Crops and Products

Abstract:With the reduction of petroleum resources and the intensification of environmental pollution, the development and application of bio-based coatings using renewable resources have become increasingly important in the wood working industry. Wood wax oil is a new bio-based natural coating that provides an environmentally friendly solution for wood preservation. The main challenges related to wood wax oil are slow drying speed and poor liquid resistance. To address this issue, wood wax oil was modified using Irgacure 2959, and the effects of the different concentrations (0, 0.5, 1.0, 1.2 and 1.5 %) of Irgacure 2959 on the properties of ultraviolet (UV) wood wax oil were explored. X-ray photoelectron of spectroscopy analysis indicated that in a wood wax oil film containing 1.2 wt% Irgacure 2959, the C–C and CO conversion rates are 15.62 % and 25.30 %, respectively. Compared with regular wood wax oil films, the 1.2 % Irgacure 2959 wood wax oil film exhibited a notable 14.2 % decrease in surface roughness. The surface of the UV wood wax oil film exhibits hydrophobic properties, which are positively correlated with its roughness. 1.2 wt% Irgacure 2959 UV-cured wood wax oil with a hardness level of 3 H, an adhesion level of 1, a viscosity of 24.87 s, and a reduction in drying time from 1 h to 20 min. The weather resistance is better than that of the commercial wood wax oil. These findings underscore the potential and versatility of UV wood wax oil, capable of forming a low-roughness and high-gloss wax film on the surface of wooden materials, thus providing an environmentally friendly and non-toxic alternative.

agronomy,agricultural engineering