Abstract:In this study, a work-of-fracture method using a three-point bend beam （3PBB） specimen, which is commonly used to determine the fracture energy of concrete, was adapted to evaluate the mode-I fracture and durability of fiber-reinforced polymer （FRP） composite-concrete bonded interfaces. Interface fracture properties were evaluated with established data reduction procedures. The proposed test method is primarily for use in evaluating the effects of freeze-thaw （F-T） and wet-dry （W-D） cycles that are the accelerated aging protocols on the mode-I fracture of carbon FRP-concrete bonded interfaces. The results of the mode-I fracture tests of F-T and W-D cycle-conditioned specimens show that both the critical load and fracture energy decrease as the number of cycles increases, and their degradation pattern has a nearly linear relationship with the number of cycles. However, compared with the effect of the F-T cycles, the critical load and fracture energy degrade at a slower rate with W-D cycles, which suggests that F-T cyclic conditioning causes more deterioration of carbon fiber-reinforced polymer （CFRP）-concrete bonded interface. After 50 and 100 conditioning cycles, scaling of concrete was observed in all the specimens subjected to F-T cycles, but not in those subjected to W-D cycles. The examination of interface fracture surfaces along the bonded interfaces with varying numbers of F-T and W-D conditioning cycles shows that （1） cohesive failure of CFRP composites is not observed in all fractured surfaces; （2） for the control specimens that have not been exposed to any conditioning cycles, the majority of interface failure is a result of cohesive fracture of concrete （peeling of concrete from the concrete substrate）, which means that the cracks mostly propagate within the concrete; and （3） as the number of F-T or W-D conditioning cycles increases, adhesive failure along the interface begins to emerge and gradually increases. It is thus concluded that the fracture properties （i.e., the critical load and fracture energy） of the bonded interface are controlled primarily by the concrete cohesive fracture before conditioning and by the adhesive interface fracture after many cycles of F-T or W-D conditioning. As demonstrated in this study, a test method using 3PBB specimens combined with a fictitious crack model and experimental conditioning protocols for durability can be used as an effective qualification method to test new hybrid material interface bonds and to evaluate durability-related effects on the interfaces.

Durability of FRP-to-concrete bonded joints subjected to 110 months accelerated laboratory and field exposure

Durability of Frp Concrete Bonds and Its Constituent Properties under the Influence of Moisture Conditions

Durability Performances of Carbon Fiber-Reinforced Polymer and Concrete-Bonded Systems under Moisture Conditions

Ultimate Strength of Reinforced Concrete Beams Retrofitted with Hybrid Bonded Fiber-Reinforced Polymer

Durability of components of FRP-concrete bonded reinforcement systems exposed to chloride environments

Long-Term Performance of External Bonding under Moisture and Temperature Effects

Bond durability of epoxy and cement- bonded CFRP reinforcement to concrete interfaces subject to water immersion

Experimental study on AFRP-to-concrete bond behavior subjected to underground water

Effects of long-term exposure of NSM CFRP-to-concrete bond to natural and accelerated aging environments

Influence of Water on Shear Bond Properties of FRP-concrete Interfaces

Long-Term Bond Durability of Fiber-Reinforced Polymer Bars Embedded in Seawater Sea-Sand Concrete under Ocean Environments

Durability of the Bond Between CFRP and Concrete Exposed to Thermal Cycles

Bond Behavior Between Basalt Fiber–Reinforced Polymer Sheet and Concrete Substrate under the Coupled Effects of Freeze-Thaw Cycling and Sustained Load

Durability of Wet Bond of Hybrid Laminates to Cast-In-Place Concrete

Mode-I Fracture and Durability of FRP-concrete Bonded Interfaces

Experimental study on the durability of FRP bars reinforced concrete beams in simulated ocean environment

Durability assessment of GFRP bars exposed to combined accelerated aging in alkaline solution and a constant load

Durability of CFRP strengthened concrete structure

Effects of Freeze-Thaw Cycles on the Behavior of the Bond Between CFRP Plates and Concrete Substrates

Investigation on damage evolution mechanism of various FRP strengthened concrete subjected to chemical-freeze-thaw coupling erosion

Bond Durability of BFRP Bars Embedded in Concrete under Seawater Conditions and the Long-Term Bond Strength Prediction