CO2 Oxidative Dehydrogenation of Propane to Olefin over Cr-M (M = Zr, La, Fe) Based Zeolite Catalyst

Mingqiao Xing,Ning Liu,Chengna Dai,Biaohua Chen

DOI: https://doi.org/10.3390/catal14060370

IF: 3.9

2024-06-08

Catalysts

Abstract:CO2 oxidative dehydrogenation of propane (CO2-ODHP), being not only favorable for olefin production but also beneficial for CO2 emission control, has recently attracted great attention. Here, a series of single metal (Cr) and bimetal (Zr, La, Fe) modified ZSM-5 zeolites were prepared via an impregnation method. It was found that the bimetal modified ZSM-5 possessed much higher C3H8 and CO2 conversion than that of monometallic modified Cr3%-ZSM-5 (Cr3%-Z5), especially for Cr3%Zr2%-ZSM-5 (Cr3%Zr2%-Z5), which displayed the highest activity (65.4%) and olefin yield (1.65 × 103 μmol·gcat−1 h−1). Various characterizations were performed, including XRD, N2 adsorption-desorption, H2-TPR, Raman, XPS, HAAD-STEM, and TEM. It was revealed that Zr not only favored an improvement in the redox ability of Cr, but also contributed to the surface dispersion of loaded Cr species, constituting two major reasons explaining the superior activity of Cr3%Zr2%-Z5. To further improve CO2-ODHP catalytic behavior, a series of Cr3%-ZSM-5@SBA-15-n composite zeolite catalysts with diverse (ZSM-5/SBA-15) mass ratios were prepared (Cr3%-ZS-n, n = 0.5, 2, 6, 16), which screened out an optimum mass ratio of six. Based on this, the Cr3%Zr2%-ZS-6 compound was further prepared, and it eventually achieved even higher CO2-ODHP activity (76.9%) and olefin yield (1.72 × 103 μmol·gcat−1 h−1). Finally, the CO2-ODHP reaction mechanism was further investigated using in situ FTIR, and it was found that the reaction followed the Mars–van Krevelen mechanism, wherein CO2 participated in the reaction through generation of polydentate carbonates. The Cr6+ constituted as the active site, which was reduced to Cr3+ after the dihydrogen reaction, and was then further oxidized into Cr6+ by CO2, forming polydentate carbonates, and thus cycling the reactive species Cr6+. Additionally, assisted by a Brönsted acid site (favoring breaking of the C-C bond), C2H4 and CH4 were produced.

chemistry, physical

What problem does this paper attempt to address?

The paper attempts to address the problem of achieving selective oxidative dehydrogenation of propane (C3H8) to produce olefins (mainly propylene C3H6) using carbon dioxide (CO2) as an oxidant, thereby improving the production efficiency of low-carbon olefins and reducing CO2 emissions. Specifically, the authors optimize catalytic performance by preparing a series of single-metal (Cr) and bimetallic (Cr with Zr, La, Fe) catalysts based on ZSM-5 zeolite, as well as composite zeolite catalysts (Cr3%-ZSM-5@SBA-15).

### Main Research Objectives:
1. **Improve Propane Conversion and Olefin Selectivity**: Enhance propane conversion and olefin selectivity by introducing auxiliary metals (such as Zr, La, Fe) and optimizing catalyst structure.
2. **Reduce CO2 Emissions**: Utilize CO2 as an oxidant, which not only aids in olefin production but also effectively reduces greenhouse gas emissions.
3. **Develop Efficient Catalysts**: Through experimental and characterization methods, reveal the active sites and reaction mechanisms of the catalysts to develop efficient CO2 oxidative dehydrogenation of propane (CO2-ODHP) catalysts.

### Research Background:
- Low-carbon olefins (such as ethylene and propylene) are important raw materials for synthesizing polymer materials and fine chemicals, which are significant for national economic development.
- With the scarcity of petroleum resources and rising oil prices, traditional processes for producing olefins from petroleum cracking need further innovation.
- Producing olefins from low-carbon alkanes (such as propane) has the advantages of low production cost, high yield, and high resource utilization efficiency.
- Traditional alkane oxidative dehydrogenation reactions are thermodynamically limited, while using CO2 as an oxidant can improve alkane conversion and olefin selectivity, while also reducing CO2 emissions.

### Research Methods:
- **Catalyst Preparation**: A series of single-metal (Cr) and bimetallic (Cr with Zr, La, Fe) modified ZSM-5 zeolite catalysts, as well as composite zeolite catalysts (Cr3%-ZSM-5@SBA-15), were prepared by impregnation method.
- **Characterization Techniques**: The catalysts were characterized using XRD, N2 adsorption-desorption, H2-TPR, Raman spectroscopy, XPS, HAADF-STEM, and TEM.
- **Reaction Performance Testing**: The propane conversion rate, CO2 conversion rate, olefin selectivity, and olefin yield of the catalysts were tested under different conditions.

### Research Results:
- **Bimetallic Modified ZSM-5 Catalysts**: Cr3%Zr2%-Z5 exhibited the highest propane conversion rate (65.4%) and olefin yield (1.65×10^3 µmol·g^-1·cat^-1).
- **Composite Zeolite Catalysts**: Cr3%Zr2%-ZS-6 showed the highest propane conversion rate (76.9%) and olefin yield (1.72×10^3 µmol·g^-1·cat^-1) at the optimal mass ratio (6:1).
- **Reaction Mechanism**: In-situ FTIR studies revealed that the reaction follows the Mars–van Krevelen mechanism, where CO2 participates in the reaction to form multidentate carbonates, with Cr6+ serving as the active site, undergoing reduction and reoxidation cycles.

### Conclusion:
The study successfully developed an efficient Cr3%Zr2%-Z5 catalyst and its composite zeolite catalyst Cr3%Zr2%-ZS-6, significantly enhancing the catalytic performance of CO2 oxidative dehydrogenation of propane, providing theoretical and technical support for the development of other efficient CO2-ODHP catalysts.