Pd@CuInP2S6 Core–Shell Nanospheres with Exceptional Hydrogen Evolution Capability and Stability in Both Alkaline and Acidic Media under Large Current Density Exceeding 1000 mA cm−2

Guoshuai Fu,Kangfan Xie,Bo Yan,Peng Yu,Xin Tan,Pu Liu,Guowei Yang

DOI: https://doi.org/10.1002/smll.202403005

IF: 13.3

2024-06-08

Small

Abstract:Schematic illustration of the synthesis of Pd@CIPS by LAL: a general strategy for fabricating uniform catalytic nanospheres with exceptional hydrogen evolution capability and stability in both alkaline and acidic media under large current density exceeding 1000 mA cm−2 By combining Pd with 2D layered crystal CuInP2S6 (CIPS) via laser irradiation in liquids, low‐loading Pd@CIPS core–shell nanospheres are fabricated as an efficient and robust electrocatalysts for HER in both alkaline and acidic media under large current density (⩾1000 mA cm−2). Pd@CIPS core–shell nanosphere has two structural features, i) the out‐shell is the nanocomposite of PdHx and PdInHx, and ii) there is a kind of dendritic structure on the surface of nanospheres, while the dendritic structure porvides good gas desorption pathway and cause the Pd@CIPS system to maintain higher HER activity and stability than that of commercial Pt/C under large current densities. Pd@CIPS exhibits very low overpotentials of −218 and −313 mV for the large current density of 1000 mA cm−2, and has a small Tafel slope of 29 and 63 mV dec−1 in 0.5 m H2SO4 and 1 m KOH condition, respectively. Meanwhile, Pd@CIPS has an excellent stability under −10 and −500 mA cm−2 current densities and 50 000 cycles cyclic voltammetry tests in 0.5 m H2SO4 and 1 m KOH, respectively, which being much superior to that of commercial Pt/C. Density functional theory (DFT) reveals that engineering electronic structure of PdHx and PdInHx nanostructure can strongly weaken the Pd─H bonding.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology