Abstract:Creep-fatigue interaction is identified as a primary failure mode for components operating under high temperatures. As operational durations extend, this interaction not only alters the material's microstructures but also initiates a gradual degradation in mechanical properties, significantly impacting its deformation and damage behaviors. In this work, the dynamic microstructural evolution of GH4169 superalloy during creep-fatigue was elucidated via qualitative characterization, and damage level evaluation method was subsequently developed by bridging microstructure degradation to mechanical property degradation. Creep-fatigue tests were performed at 650 °C with various tensile holding times and were interrupted at lifetime fractions of 10 %, 50 % and 80 % for further analysis and tensile evaluations. Results revealed that the prolonged exposure to holding times induced the coarsening of γ″ precipitates alongside an increase in low-angle grain boundaries, culminating a reduction in creep-fatigue strength. The development of voids and cracks exacerbated the degradation of elongation, leading to a hybrid fracture mode encompassing both intergranular and transgranular cracking paths. Synthesizing microstructural evolutions to qualitatively categorize diverse degradation levels imparted a robust physical basis for damage evaluation. A mapping model was established to correlate the average kernel average misorientation (micro-degradation indicator) with the tensile plastic strain energy density (macro-degradation indicator). The damage level evaluation method was endowed with quantitative metrics utilizing this model, and its generality was additionally validated in P92 steel. This work offers an insight into the quantitative damage evaluations of creep-fatigue-induced degradations in materials, thereby providing a theoretical basis for the development of operation management and inspection plans of components.

Understanding the relation between creep-fatigue fracture mechanisms and intergranular dislocation accommodation of a high chromium steel using nanoindentation characterization

Characterization of the Cyclic Softening and Remaining Creep Behaviour of P92 Steel Weldment

Study on Creep Behavior and Fracture Life Prediction Method of P92 Steel Based on Finite Element Analysis

An Insight into the Creep-Fatigue Damage Localization in Welded Joints Based on Crystal Plasticity Finite Element Method

Damage behaviour in different micro-regions of P92 steel weldment under sequential low cycle fatigue and creep loading

Remaining creep properties and fracture behaviour of P92 steel welded joint under prior low cycle fatigue loading

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Nanoindentation characterization on the temperature-dependent fracture mechanism of Chinese 316H austenitic stainless steel under creep-fatigue interaction

Probing strain rate effect on the creep–fatigue fracture mechanism of 9%Cr steel‐welded joint via nanoindentation characterization

Fatigue-Creep Interaction Of P92 Steel And Modified Constitutive Modelling For Simulation Of The Responses

The correlation between prior fatigue damage and remaining creep properties in a high chromium steel welded joint

The Relative Significance of Internal Damage Mechanisms on the Overall Creep Damage and Ultimate Failure of P91 Steel

The Effects of Tensile and Compressive Dwells on Creep-Fatigue Behavior and Fracture Mechanism in Welded Joint of P92 Steel

Evaluation of the Effect of Various Prior Creep-Fatigue Interaction Damages on Subsequent Tensile and Creep Properties of 9%cr Steel

Creep-Fatigue Crack Initiation Simulation of a Modified 12% Cr Steel Based on Grain Boundary Cavitation and Plastic Slip Accumulation

Insight into the creep-fatigue interaction and remaining creep damage mechanisms in different micro-regions of 9%Cr steel welded joints

Experimental and Numerical Characterization of Low Cycle Fatigue and Creep Fatigue Behaviour of P92 Steel Welded Joint

Microstructural Damage Mechanics-Based Model for Creep Fracture of 9%cr Steel under Prior Fatigue Loading

Semi-quantitative creep-fatigue damage analysis based on diffraction-based misorientation mapping and the correlation to macroscopic damage evolutions

Creep-fatigue Damage Level Evaluation Based on the Relationship Between Microstructural Evolution and Mechanical Property Degradation

Creep-fatigue interactive behavior and damage mechanism of TP321 stainless steel under hybrid-controlled conditions