Structural, optical, and radiation shielding parameters of zinc silicate glasses modified with erbium oxide

M. El Baiomy,R.M. Ramadan,Y.M. Moustafa,G. El Damrawi

DOI: https://doi.org/10.1016/j.optmat.2024.115529

IF: 3.754

2024-05-22

Optical Materials

Abstract:Zinc silicate glasses containing varying concentrations of Er 2 O 3 with the composition xEr 2 O 3 . (55-x)ZnO.45SiO 2 were produced using the widely used MELT ANNEALING TECHNIQUE. XRD spectroscopy was utilized to validate the absence of a defined crystalline structure in the prepared samples. The optical characteristics of the samples were analyzed by ultraviolet (UV), visible (Vis), and photoluminescence (P L ) spectroscopies. Various spectral peaks were observed in different spectral regions, indicating the electronic transitions from the lower (ground) state to various higher (excited) states of Er 2 O 3 . The Davis-Mott relation calculates the optical energy gap (E g ) based on the absorption spectra. With the addition of Er 2 O 3 , E g values range from 2.26 to 3.09 eV for indirect band gaps and from 2.8 to 3.17 eV for direct band gaps. Adding Er 2 O 3 to the glasses resulted in significant improvements in several optical properties. Specifically, the absorption spectra, refractive index, penetration depth, extinction coefficient, absorption coefficient, optical conductivity, and dielectric constant were all enhanced. The utilization of Er 2 O 3 led to an increase in both the absorption and emission cross-sections, as well as the cross-sectional gain of the glasses. As the concentration of Er 2 O 3 increases, the glasses' refractive indices fluctuate between 2.35 and 2.53, while the emission cross-section increases from 4.037 × 10 −22 to 2.65 × 10 −21 cm 2 . Photoluminescence data was obtained by exciting the glasses with a 980 nm pump wavelength, and it was found that the glasses exhibited superior luminescence emission at 1350 nm. Density (D) and molar volume (V m ) show the same increasing behaviors, which led to suggest that changing the glass structure, the size of well-modified structural units modified via Er 2 O 3 addition. Oxygen packing (OP d ) and oxygen molar volume (OV m ) show an inverse relation which predict formation of non-bridging oxygen upon addition of Er 2 O 3 . The Phy-X/PSD application evaluated the generated samples' radiation shielding properties. The assessment was carried out in the energy spectrum between 0.015 and 15 MeV. As the concentration of Er 2 O 3 increased, the samples' mass and linear attenuation coefficients also increased while the half-value layer (HVL) decreased. These findings suggest that the glass matrix has significant potential for optoelectronic and shielding applications.

materials science, multidisciplinary,optics