Boosting the activation of molecular oxygen and the degradation of tetracycline over high loading Ag single atomic catalyst
Zhiruo Zhou,Zhurui Shen,Chunlin Song,Mingmei Li,Hui Li,Sihui Zhan
DOI: https://doi.org/10.1016/j.watres.2021.117314
IF: 12.8
2021-08-01
Water Research
Abstract:<p>Photocatalytic activation of molecular oxygen (O<sub>2</sub>) is a promising way in oxidative degradation of organic pollutants. However, it suffers from low efficiency mainly due to the limited active sites for O<sub>2</sub> activation over traditional photocatalysts. Therefore, we established a single atomic Ag-<em>g</em>-C<sub>3</sub>N<sub>4</sub> (SAACN) catalyst with 10 wt% loading of Ag single sites for boosting the O<sub>2</sub> activation during the degradation of tetracycline (TC), and 10 wt% loading of nanoparticle Ag-<em>g</em>-C<sub>3</sub>N<sub>4</sub> (NPACN) was studied as a comparison. When using SAACN, the accumulative concentration of superoxide (•O<sub>2</sub><sup>−</sup>), hydroxyl radical (•OH), singlet oxygen (<sup>1</sup>O<sub>2</sub>) reached up to 0.66, 0.19, 0.33 mmol•L<sup>−1</sup>•h<sup>−1</sup>, respectively, within 120 min, 11.7, 5.7 and 4.9 times compared with those using NPACN, representing 17.24% of dissolved O<sub>2</sub> was converted to reactive oxygen species (ROS). When additionally feeding air or O<sub>2,</sub> the accumulative concentrations of •O<sub>2</sub><sup>−</sup>, •OH, <sup>1</sup>O<sub>2</sub> were even higher (air: 4.21, 0.97, 2.02 mmol•L<sup>−1</sup>•h<sup>−1</sup>; O<sub>2</sub>: 17.13, 1.32, 9.00 mmol•L<sup>−1</sup>•h<sup>−1</sup>). The rate constants (<em>k</em>) for degrading the TC were 0.0409 min<sup>−1</sup> over SAACN and 0.00880 min<sup>−1</sup> over NPACN, respectively (mineralization rate: 95.7% <em>vs.</em> 59.9% after 3 h of degradation). Moreover, the degradation ability of SAACN did not decrease in a wide range of pH value (4-10) or under low temperature (10 °C). Besides the high exposure of Ag single sites, other advances of SAACN were: 1(O<sub>2</sub> was more energetic favorable to adsorb on single atomic Ag sites; 2) Positive Ag single sites were easier to obtain the electrons from the surrounding N atoms, and facilitated electron transfer towards adsorbed O<sub>2</sub>.</p>
environmental sciences,engineering, environmental,water resources