Fabricating Spinel-Type High-Entropy Oxides of (Co, Fe, Mn, Ni, Cr)3O4 for Efficient Oxygen Evolution Reaction
Xiaofei Hao,Ran Wang,Xiumin Tan,Xiufeng Zhang,Xupo Liu,Zhaoyang Wu,Dongli Yuan
DOI: https://doi.org/10.3390/ma17143415
IF: 3.4
2024-07-11
Materials
Abstract:Fabricating efficient oxygen evolution reaction (OER) electrocatalysts is crucial for water electrocatalysis. Herein, the spinel-type high-entropy oxides of (Co, Fe, Mn, Ni, Cr)3O4 were synthesized through the high-temperature calcination approach. The influences of calcination temperatures on structures and electrochemical properties were investigated. The optimized catalyst of HEO-900 contains the hybrid structure of regular polyhedrons and irregular nanoparticles, which is beneficial for the exposure of electrochemically active sites. It was identified that the abundant high-valence metal species of Ni3+, Co3+, Fe3+, Mn4+, and Cr3+ are formed during the OER process, which is generally regarded as the electrochemically active sites for OER. Because of the synergistic effect of multi-metal active sites, the optimized HEO-900 catalyst indicates excellent OER activity, which needs the overpotential of 366 mV to reach the current density of 10 mA cm−2. Moreover, HEO-900 reveals the prominent durability of running for 24 h at the current density of 10 mA cm−2 without clear delay. Therefore, this work supplies a promising route for preparing high-performance multi-metal OER electrocatalysts for water electrocatalysis application.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering