Hydrothermal synthesis of MgCO3 and its optical properties
Shibing Ni,Tao Li,Xuelin Yang
DOI: https://doi.org/10.1016/j.jallcom.2011.04.064
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:Well-crystallized magnesium carbonate micro-particles were successfully synthesized by a simple hydrothermal method. The structure of the as-synthesized products was characterized by X-ray diffraction (XRD), which is in good agreement with hexagonal rhomb-centered MgCO 3 . Field emission scanning electron microscopy (FE-SEM) characterization indicates that the as-synthesized MgCO 3 micro-particles are of mean size about 30 μm. The photoluminescence properties of the as-synthesized MgCO 3 were measured at room temperature, which shows wide emissions with three emission centers ranging from violet to red. The violet emission center locates at 425 nm, the green emission center locates at 550 nm, and the red emission center locates at 698 nm. Keywords Ceramics Composite materials Magnesium carbonate Crystal growth Photoluminescence 1 Introduction Magnesium carbonate (MgCO 3 ) has attracted much attention for many years due to its wide applications in diverse areas such as rubber industry, medicine, thermal insulating fillers, active starting materials of magnesia or carbon nanotubes, minerals, and seawater treatment [1–10] . Stimulated by those applications, different methods such as solid reaction, precipitation, and water bath were developed to synthesize MgCO 3 [11–13] . However, those researches have mainly focused on morphology controlled fabrication and growth process investigation. To the best of our knowledge, no research about the photoluminescence properties of MgCO 3 was reported by now. The main object of this paper is to develop a simple method to synthesize MgCO 3 and to research its photoluminescence properties. 2 Experimental All the chemicals were analytical grade and purchased from Tianjing Chemical Reagents. In a typical process, 2.5 mmol hexamethylenetetramine, 2.5 mmol magnesium acetate, and 0.5 g sodium sulfate were dissolved in 30 ml distilled water. After stirring for 20 min, the obtained homogeneous solution was transferred into a 50 ml-teflonlined autoclave, distilled water was subsequently added to 80% of its capacity. The autoclave was at last sealed and placed in an oven, heated at 160 °C for 24 h. The precipitate was washed with distilled water and ethanol for 4 times at 6000 rpm for 5 min. Finally the resulting products were dried in an oven at 60 °C for 24 h. The structure and morphology of the products were characterized by X-ray powder diffraction (Rigaku RINT2400 with Cu Kα radiation), field-emission scanning electron microscopy (FE-SEM S-4800, Hitachi), and micro-Raman spectrometer (Jobin Yvon LabRAM HR800 UV, YGA 532 nm). The UV–vis reflection spectrum was characterized by Ultraviolet–visible spectrophotometer (Shimadzu UV3600) using an integrating sphere. Room temperature PL was measured on micro-Raman spectrometer (Jobin Yvon LabRAM HR800 UV, He–Cd 325 nm). 3 Results and discussion The typical X-ray diffraction pattern of the as-synthesized products is shown in Fig. 1 . All diffraction peaks can be indexed as the hexagonal phase of MgCO 3 with Rhomb-centered lattice constants a = 0.4633 nm, c = 1.501 nm, which is in good agreement with the JCPDS, No. 08-0479. Strong and sharp peaks suggest that the as-synthesized products are well crystallized. The reactions during the hydrothermal process are likely to be as follows: (1) (CH 2 ) 6 N 4 + 10H 2 O → 6HCHO + 4NH 3 ·H 2 O (2) HCHO + O 2 → CO 2 + H 2 O (3) CO 2 + H 2 O → CO 3 2− + 2H + (4) Mg 2+ + CO 3 2− → MgCO 3 Fig. 2 (a) shows a low magnification SEM image of MgCO 3 micro-particles. It can be seen that the as-synthesized MgCO 3 consists of a large number of micro-particles with big size and a small quantity of particles with small size. The size of those particles ranges from hundreds of nanometers to tens of micrometers, and the mean size of those micro-particles is about 30 μm. High magnification SEM image of the as-synthesized MgCO 3 is shown in Fig. 2 (b). It can be seen clearly that there are some small-sized particles on the surface of MgCO 3 micro-particles. The mean size of those small particles is about 2 μm, and the micro-particles are of smooth surfaces with size about 30 μm. As shown in Fig. 3 , Raman spectrum of MgCO 3 in the wavelength range of 150–1500 cm −1 are dominated by the peaks located at 321, 476, 746, 899, and 1107 cm −1 , and these peaks are the vibration bands of MgCO 3 . The peaks at 746 and 1107 cm −1 are caused by the in-plane bending and symmetry-related stretching vibration, and the peak at 321 cm −1 comes from librational motion of the carbonate groups relative to the divalent cation [9,13–15] . The weak peak at 476 cm −1 comes from Mg–O vibration, whereas the weak peak at 899 cm −1 originates from SO 4 2− [16,17] . Fig. 4 displays the UV–vis reflection of the as-synthesized MgCO 3 . The reflection spectrum of MgCO 3 shows a high reflection (>70%) in the region from 450 to 900 nm, and then fell sharply in the region from 300 to 450 nm due to the onset of fundamental absorption. The optical band gap energy (Eg) was estimated by the method proposed by Wood and Tauc [18] . According to these authors the optical band gap is associated with absorbance and photon energy by the following equation: h ν α ∝ ( h ν − Eg ) 2 where α is the absorbance, h is the Planck constant, ν is the frequency, and Eg is the optical band gap. In this case, the Eg value of MgCO 3 powders is evaluated by extrapolating the linear portion of the curve ( αhν ) 1/2 vs hν . The obtained results are shown in insert of Fig. 4 , exhibiting an indirect band gap semiconductor with band gap value of 2.89 eV (429 nm). The band gap value evaluated from UV–vis reflection is smaller than that obtained from first principle calculation [19–21] . The divergence between these two methods is likely due to the size or morphology related surface defects. Fig. 5 shows the PL spectrum of MgCO 3 that measured at room temperature using an excitation wavelength of 325 nm. A wide range of visible light emission that ranges from violet to red can be found in the PL spectrum. There are three emission centers in visible light region, which consist of the violet emission center located at 425 nm, the green emission center located at 550 nm, and the red emission center located at 698 nm, respectively. Considering the band gap value of MgCO 3 (2.89 eV) that evaluated from UV–vis reflection spectrum, one can deduce that the violet emission center of MgCO 3 located at 425 nm may be relevant to the electron transition from the conduction band to valence band of MgCO 3 , which is in accordance with the indirect electronic band gap along Γ to M direction [19] . In addition, it has been well recognized that local defects such as atom vacancies or interstitials may induce new energy levels in the band gap [22,23] . MgCO 3 was fabricated in hydrothermal environment, defects such as O vacancies, Mg vacancies, or Mg interstitials can inevitably be formed. As the energy of the green and red emission centers (2.26 eV and 1.78 eV) are smaller than the band gap value evaluated from UV–vis reflection spectrum, it can be deduced that defects in MgCO 3 are due to the green and red emissions. The wide region of visible light emission of MgCO 3 endows it with promising application in optical field. 4 Conclusions In conclusion, MgCO 3 micro-particles with mean size of about 30 μm were synthesized by a simple hydrothermal method. The structure and morphology of MgCO 3 micro-particles were characterized by X-ray diffraction, Raman spectrum, and field emission scanning electron microscopy. The photoluminescence properties of MgCO 3 micro-particles were characterized at room temperature, which shows wide region of visible light emission from violet to red. This wide region PL behavior endows it with potential applications in optical field. Acknowledgements We gratefully acknowledge the financial support from Natural Science Foundation of China (NSFC, 50972075), key projects of Chinese Ministry of Education (D209083), and Education Office of Hubei Province (D20081304 and CXY2009A004). Moreover, the authors are grateful to Dr. Jianlin Li at Three Gorges University for his kind support to our research. References [1] A. Botha C.A. Strydom Hydrometallurgy 62 2001 175 [2] X.L. Wang D.F. Xue C.L. Yan Chem. Technol. Market 29 2006 28 [3] F. Freitag P. Kleinebudde Eur. J. Pharm. Sci. 19 2003 281 [4] Z.P. Zhang Y.J. Zheng Y.W. Ni Z.M. Liu J.P. Chen X.M. Liang J. Phys. Chem. B 110 2006 12969 [5] Z.P. Zhang Y.J. Zheng J.X. Zhang Q. Zhang J.P. Chen Z.M. Liu Cryst. Growth Des. 7 2007 337 [6] K. Mitsuhashi N. Tagami K. Tanabe T. Ohkubo H. Sakai M. Koishi Langmuir 21 2005 3659 [7] T. Ohkubo S. Suzuki K. Mitsuhashi T. Ogura S. Iwanaga H. Sakai Langmuir 23 2007 5872 [8] Z.S. Lou C.L. Chen Q.W. Chen J. Phys. Chem. B 109 2005 10557 [9] A. Wang J.D. Pasteris H.O.A. Meyer M.L. Dele-Duboi Earth Planet. Sci. Lett. 141 1996 293 [10] S.M. Stanley Chem. Rev. 108 2008 4483 [11] G.L. Gao W.L. Zhang H.B. Li L.M. Lang Z. Xu Cryst. Growth Des. 8 2008 3785 [12] K. Sandengen L.O. Jøsang B. Kaasa Ind. Eng. Chem. Res. 47 2008 1002 [13] Z. Xing Q. Hao Z.C. Ju L.Q. Xu Y.T. Qian Mater. Lett. 64 2010 1401 [14] Z.S. Lou Q.W. Chen Y. Zhu Y.F. Zhang J. Gao Cryst. Growth Des. 4 2004 415 [15] R.G. Herman C.E. Bogdan A.J. Sommer D.R. Simpson Appl. Spectrosc. 41 1987 437 [16] R.N. Gayen S.N. Das S. Dalui R. Bhar A.K. Pal J. Cryst. Growth 310 2008 4073 [17] C.F. Windisch J.J.L. Cox E.N. Greenwell Spectrochim. Acta, Part A 53 1997 1981 [18] D.L. Wood J. Tauc Phys. Rev. B 5 1972 3144 [19] F.M. Hossain B.Z. Dlugogorski E.M. Kennedy I.V. Belova G.E. Murch Solid State Commun. 150 2010 848 [20] M.G. Brik Physica B 406 2011 1004 [21] A.R. Oganov S. Ono Y.M. Ma C.W. Glass A. Garcia Earth Planet. Sci. Lett. 273 2008 38 [22] H.B. Zeng W.P. Cai Y. Li J.L. Hu P.S. Liu J. Phys. Chem. B 109 2005 18260 [23] H.B. Zeng G.T. Duan Y. Li S.K. Yang X.X. Xu W.P. Cai Adv. Funct. Mater. 20 2010 561