Synthesis of Metal Oxide Nanoparticles by Rapid, High‐Temperature 3D Microwave Heating
Geng Zhong,Shaomao Xu,Chaoji Chen,Dylan Jacob Kline,Michael Giroux,Yong Pei,Miaolun Jiao,Dapeng Liu,Ruiyu Mi,Hua Xie,Bao Yang,Chao Wang,Michael R. Zachariah,Liangbing Hu
DOI: https://doi.org/10.1002/adfm.201904282
IF: 19
2019-09-19
Advanced Functional Materials
Abstract:<p>Microwave‐assisted fabrication has propelled the recent synthesis and processing approaches of various nanomaterials. However, in most previous studies, the synthesis temperature is limited to below 1100 K, which restricts its application. Here, a rapid, in situ 3D heating method to manufacture well‐dispersed metal oxide nanoparticles on a 3D carbonized wood (denoted as C‐wood) host using microwaves as the driving power is reported. The moderate electronic conductivity of C‐wood contributes to the local Joule heating and the good thermal conductivity guarantees the rapid 3D heating of the overall material. The temperature of the C‐wood increases from room temperature to ≈2200 K in 4 s (≈550 K s<sup>−1</sup>), stabilizing to 1400 K, and then cooling back down to room temperature within 2 s. The preloaded precursor salts rapidly decompose and form ultrafine (≈11 nm) metal oxide nanoparticles on the surface of the C‐wood during the rapid quenching. The process takes place in air, which helps prevent the metal oxides from being reduced by the carbon. The 3D heating method offers an effective route to the rapid and scalable synthesis of metal oxide nanoparticles.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology