Ethanolamine piezoelectric hydrogels structured by oleic acid lamellae

Erica Pensini,Stefano Gregori,Alejandro G. Marangoni,Saeed Mirzaee Ghazani,Zhangfei Su,Aicheng Chen,Nour Kashlan

DOI: https://doi.org/10.1016/j.molliq.2024.124185

IF: 6

2024-02-06

Journal of Molecular Liquids

Abstract:Ethanolamine and ultrapure water have negligible electrical conductivity, whereas their mixtures are electrically conductive. Their electrical conductivity is maximum with ≈20 wt% (≈7 mol%) ethanolamine relative to water, suggesting the formation of conductive ethanolamine-water clusters. Current vs. voltage curves measured during cyclic voltammetry experiments display negligible hysteresis with ethanolamine-water mixtures, which are liquid at 200C. Ethanolamine interacts with oleic acid at a 1:1 mol ratio to produce a solid, where oleic acid is self assembled into lamellar phases, as shown by X ray diffraction (XRD). Lamellae arrange themselves into ribbons, as seen by polarized light microscopy. These ribbons are also seen upon addition of water. Shear rheology shows that mixtures containing 90 wt% water and equimolar amounts of oleic acid and ethanolamine are gels between frequencies of 1–100 rad/s. At 6 rad/s, the ratio between the storage modulus G' and the loss modulus is G" is ≈4.5. With either 64 wt% or 95 wt% water, gels are plastic at lower strains. Polarization modulation infrared reflection–absorption spectroscopy shows that the sign of applied electric potentials affects the orientation of oleic acid acyl chains on a gold surface. Also, polarized light microscopy images reveal that mechanical stresses develop in the gels when they are subjected to electric fields. This is because gels are piezoelectric, as shown by cyclic voltammetry experiments, and when they are compressed, electric current flows through them. The current decay is faster with a molar excess of oleic acid, because gels are mechanically weaker and therefore relax faster.

chemistry, physical,physics, atomic, molecular & chemical