Abstract:In this paper, We prepared two groups of the glasses, the first group is Ge x As 20 Se 80-x with x from 5 % to 32.5 %, the second group is Ge x Sb 20 Se 80-x with x from 5 % to 25 %, using the conventional melt-quench method, and investigated the effect of the elemental substitution of As by Sb on the threshold behaviors in Ge x As(Sb) 20 Se 80-x glasses. We aimed to understand that,to which degree the topological model and chemical order model can explain the correlation between the physical properties and glass compositions, and how the chemical composition can affect the transition threshold in the glasses. Glass transition temperature was measured by the differential scanning calorimeter (Mettler-Toledo, DSC1) with different scanning rates from 5 K/min to 30 K/min under a uniform nitrogen gas flow of 50 mL/min, the density of the glasses was measured by a Mettler H20 balance with a MgO crystal used as a reference. Samples from each glass composition were weighed five times and the average density was recorded, the refractive index of the glass at 1.5 um was measured by a Metricon Model 2010 prism coupler. Raman spectra were measured from a T64000 Jobin-Yvon-Horiba micro-Raman spectrometer equipped with a liquid-nitrogen-cooled CCD detector. The 830 nm laser line was used as an excitation source, and the laser power was kept as small as possible to avoid any photo-induced effects. The resolution of the spectrometer was about 0.5 cm -1 . The result from systematic measurements of these physical parameters shows that, while the transition thresholds at MCN=2.4 and 2.67 were verified in the Ge-As-Se glasses with ideal covalent network, these two transitions represent the covalent network structure inside the glass from an under-constrained “floppy” network to an over-constrained “rigid” phase and from the two-dimensional to the three-dimensional “stressed rigid” phase respectively. However, when As is substituted by Sb, the Ge x Sb 20 Se 80-x glass with non-ideal covalent network will change of the transition thresholds, which changes to the chemically stoichiometric composition. We further deconvolved Raman scattering spectra into different structural units and the change of their respective intensity showed the same behavior, and this was ascribed to the chemical effect induced by a large difference of the atomic radius between As and Sb, and a relatively strong ionic feature of the element Sb.

Influence of silver introduction on glass-transition and crystallization processes in As40Se30Te30 glass

Kinetics of thermally induced processes in Ag doped As40Se30Te30 chalcogenide glass

Effects of Ag Additive on Structure and Crystallization Behaviors of As2(Se15Te85)3 Glasses

Influence of quenching rate on the crystallization behaviors of Mg63Ni22Pr15 metallic glass

Impact of Ag, Bi, Cd, and Zn incorporation on the kinetic parameters of glass transition/crystallization in chalcogens Se- and Te-rich ternary glass

Study on Crystallization Behavior of Novel Silver Chloride Based Chalcogenide Glasses

Crystallization Behaviors of Glasses in the (Ge5sb25se70)1-Xagx System

Crystallization kinetics of Si15Te85 and Si20Te80 chalcogenide glasses

Mutual effects of Ag doping and non-stoichiometric glass forming units on the structural, thermal, and electrical properties of Ag30+xAs28-xSe21Te21 chalcogenide glasses

Effects of the Se Substitution for Te on the Structure and Properties of Glasses in the Ag30As28(SexTe100-x)42 System

Effects of Ag Addition on Properties and Structure of Ge–Ga–Se–AgI Chalcohalide Glasses

Thermal, structural, and conductivity properties of As14Sb26S(60−x)–(AgI)x chalcogenide glasses

Ab initio determination of ion-traps in silver-doped chalcogenide glass

Thermal stability and crystallization kinetic of Se-Te-Ag glassy alloys and thick films for electronic devices

Sintering of a Crystallizable CaO‐B2O3‐SiO2 Glass with Silver

Amorphous to Amorphous Insulator-Metal transition in GeSe$_3$:Ag glasses

Crystallization Kinetics in Cu35ag15zr45al15 Metallic Glass

Investigation of the substitution of mercury by silver in Ag 2 S-HgS-GeS 2 glasses: Macroscopic, electrical and vibrational properties

Unraveling the influence of some foreign elements on microhardness and thermomechanical characteristics of SeTeSn alloy

Tuning crystallization kinetics by high-content solvent element substitution between Cr45Fe11Co7Mo14C15B6Y2 and Fe41Cr15Co7Mo14C15B6Y2 metallic glasses

Effect of the elemental substitution on threshold behaviours in Ge-As(Sb)-Se glasses