Abstract:The research explores the possibility of utilizing carbon dioxide to modify the properties of recycled brick powder (RBP) and enhance the engineering performances of RBP-mortar. The RBP, crushed to the size range of 0.075 to 4 mm, is carbonated by exposing to 5% CO2 for 4 h and characterized for phase composition, porosity and micro-structure. The non-carbonated RBP (RBP) and pre-carbonated RBP (Carb-RBP) are applied to replace 25% and 75% of manufactured sand (M-sand) in cement mortars maintained at similar flow level (110 – 113%), which are then cured under three conditions - (i) ambient condition (N), (ii) 4 h of steam curing followed by moist and dry curing (STC), and (iii) accelerated CO2 curing (5% CO2 of 99% purity) for 4 h followed by moist curing and dry curing (CC). Physico-chemical characterizations suggest that Carb-RBP has higher micro-pore volume and surface area contributed by pores in the size range of 1 nm to 3 nm than RBP. After carbonation, the reactivity of RBP in alkaline environment is increased due to CO2-induced breakdown of calcium and alumino-silicate minerals into calcium carbonate and silica gel. Due to addition of 25% and 75% RBP and Carb-RBP, hydration kinetics is accelerated by 4 – 4.50 h compared to control due to nucleation of hydration products on the surfaces of RBP. Faster precipitation of hydration products, more micro-pore sites in RBP and higher porosity due to increased water demand enhance the carbon sequestration in RBP-mortars and Carb-RBP mortars by 30–82% compared to control (0% RBP). Use of Carb-RBP to replace 25% of M-sand offer similar compressive strength as control and 19 – 21% higher strength than mortars with RBP (non-carbonated). CO2 curing also reduces the total shrinkage of mortars with recycled brick powder by 12 – 17% compared to ambient curing and steam curing due to densification by calcium carbonate crystals. The findings from this research strongly suggests a significant reduction in embodied carbon of Portland cement-based construction materials by utilizing a combined approach of carbon sequestration and replacement of fine aggregates by recycled brick powder.

Amine-Functionalized Carbonate Mortars of CO2 Absorption for Carbon Neutrality and Enhanced Rebar Corrosion Resistance

Enhanced Carbonation Curing of Cement Pastes with Dolomite Additive

Steel Corrosion and Corrosion-Induced Cracking in Reinforced Concrete with Carbonated Recycled Aggregate

Study on CO2 Absorption-Mineralization Characteristics of Mixed Amine Solution Coupled with CaO and Key Influencing Factors in Mineralization Process

Development of Carbon Capture Coating to Improve the Durability of Concrete Structures

Sustainable Building Material from CO2 Mineralization Slag: Aggregate for Concretes and Effect of CO2 Curing

Carbon dioxide sequestration in mortars with excavated soil: Engineering performances and environmental benefits

Improved chloride binding capacity and corrosion protection of cement-based materials by incorporating alumina nano particles

Chloride Ions' Penetration of Fly Ash and Ground Granulated Blast Furnace Slags-Based Alkali-Activated Mortars

Carbon dioxide as an admixture for better performance of OPC-based concrete

Approaches to enhance the carbonation resistance of fly ash and slag based alkali-activated mortar- experimental evaluations

Accelerating the Reaction Kinetics of Na2CO3-Activated Slag Mortars by Calcined Recycled Concrete Fines

Steel Corrosion Behavior of Reinforced Calcium Aluminate Cement-Mineral Additions Modified Mortar

Research Progress in Corrosion Mechanism of Reinforced Alkali-Activated Concrete Structures

Effects of reactive MgO on durability and microstructure of cement-based materials: Considering carbonation and pH value

Innovative use of solid CO2 as an eco-friendly additive in alkali-activated concrete for enhancing its performance

Synergetic effect of CO 2 curing and bottom ash with low Ca on the enhancement of carbonation behavior and mechanical performance

Strength, Fracture and Durability Characteristics of Ambient Cured Alkali—Activated Mortars Incorporating High Calcium Industrial Wastes and Powdered Reagents

Sequestration and utilization of carbon dioxide to improve engineering properties of cement-based construction materials with recycled brick powder: a pathway for cleaner construction

A renewable admixture to enhance the performance of cement mortars through a pre-hydration method

Effect of borax-modified activator on mechanical properties and drying shrinkage of alkali-activated slag/metakaolin mortar