Facile synthesis of hybridized triple-shelled hollow mesoporous organosilica nanoparticles

Ruifa Yu,Jun Tao,Lixin Shao,Wei Lu,Jiajia Zhao,Rui Tang,Jing Li,Zhaogang Teng

DOI: https://doi.org/10.1016/j.jtice.2021.10.022

IF: 5.477

2022-02-01

Journal of the Taiwan Institute of Chemical Engineers

Abstract:Background Multilayer hollow materials have attracted considerable attention as potentially valuable in drug delivery, catalysis, and nanoreactors. The main purpose of this work is to synthesize hybridized triple-shelled hollow mesoporous organosilica nanoparticles (htHMONs) with ethane-, benzene-, and thioether groups. Methods The nanoparticles are prepared using a surfactant-directed co-assembly process and a following hydrothermal etching strategy. First, hybridized mesostructured organosilica nanoparticles were synthesized via step-by-step adding multiple organosilica in a surfactant solution. The mesostructured organosilica nanoparticles are then transformed into htHMONs by hydrothermal treatment at 160 °C for 3 h. Finding The prepared typical htHMONs possess a uniform diameter (320 nm), independent core (107 nm), and three separate shells (10, 13, and 23 nm from outside to inside). In addition, htHMONs possess typical properties of mesoporous materials, including uniform mesopore (4.20 nm), large specific surface area (SSA) (458 m2g−1), and huge pore volume (0.82 cm3g−1). Furthermore, htHMONs with various sizes (190–330 nm) are also prepared by varying the amount of structure-directing agent or volume ratio of water to ethanol.

engineering, chemical