Abstract:Phenolic resins occupy an important position in industrial applications, but phenol, one of the raw materials for synthesis, is a non-renewable resource. Lignin, as a natural polymer containing phenolic hydroxyl groups, alcohol hydroxyl groups and other reactive groups, can replace some of the phenol in the synthesis of phenolic resins, which can reduce the amount of phenol, thus reducing the cost of phenolic resins, while effectively promoting the high value-added use of renewable biomass resources. Due to its low reactivity, alkaline lignin is usually discharged as production waste, unaware that lignin macromolecules can be modified. In this paper, the phenolic monomers were obtained by acid-catalyzed depolymerization of DES (choline chloride/p-toluenesulfonic acid or choline chloride/lactic acid) from waste alkaline lignin, and the recovery rate of the DES solution during the catalytic treatment was more than 85 %, in which the main monomer was 2-methoxy-4-(1-propyl) phenol. The degradation of alkaline lignin is still favorable after five times of DES solvent recovery. The depolymerized lignin monomer replaced phenol by 50 wt% and then ternary co-polymerized with phenol and formaldehyde to form a biomass phenol-based phenolic resin, providing a green route for phenolic resin production. The cost of resin preparation was economically calculated, and it was found that the cost of resin after accumulating 4 cycles of DES treatment was only 51.1 % of that of pure phenolic resin. The density functional theory (DFT) was used to simulate the possible radical reactions in the intermediate process of phenolic resin reaction, to explore the microscopic mechanism and competition, to provide theoretical reference for further experimental realization of resin structure control and optimization, and to improve the theoretical system of resin synthesis.

Polymerization of α-pinene catalyzed by Lewis acidic deep eutectic solvents

Polymerization of 1,3-Butadiene Catalyzed by Ion-Pair Cobalt Complexes with (benzimidazolyl)pyridine Alcohol Ligands

Lewis acidic deep eutectic solvents as catalysts for rosin polymerization

Advanced Catalyst Technology for Broad/Bimodal Polyethylene, Achieved by Polymer-Coated Particles Supporting Hybrid Catalyst

Solvent effect on cis-1,4-specific polymerization of 1,3-butadiene with CoCl2(PRPh2)2–EASC catalytic systems

ETHYLENE POLYMERIZATION WITH CORE-SHELL ZIEGLER-NATTA HYBRID CATALYSTS

Palladium/Benzoic Acid-Catalyzed Regio- and Stereoselective Polymerization of Internal Diynes and Diols Through C(sp(3))-H Activation

Efficient heterogeneous functionalized polymer ionic liquid catalyst for the synthesis of ethylene carbonate via the coupling of carbon dioxide with ethylene oxide

Promoting Ethylene (co)Polymerization in Aliphatic Hydrocarbon Solvents Using tert ‐Butyl Substituted Nickel Catalysts

Study on the kinetics ofα-pinene hydration

Characterization and properties of phenolic resin doped modified lignin

A paradigm for the efficient synthesis of bio-based polycarbonate with deep eutectic solvents as catalysts by inhibiting the degradation of molecular chains

Mechanism of synergistic effects and kinetic analysis in bamboo-LDPE waste <i>ex</i>-<i>situ</i> catalytic co-pyrolysis for enhanced aromatic hydrocarbon production via CeZrAl and HZSM-5 dual catalyst

Amino acid-based deep eutectic solvent induced catalyst self-separation of ethylene alkoxycarbonylation: An experimental and computational study

Ternary deep eutectic solvents for esterification of 2-methylpropenoic acid with alcohols

Aqueous-phase Biphasic Dehydroaromatization of Bio-Derived Limonene into P-Cymene by Soluble Pd Nanocluster Catalysts

Lewis Acid-Facilitated Deep Eutectic Solvent (DES) Pretreatment for Producing High-Purity and Antioxidative Lignin

Preparation of amphiphilic mesoporous carbon-based solid acid from kraft lignin activated by phosphoric acid and its catalytic performance for hydration of α-pinene

Catalytic depolymerization of Camellia oleifera shell lignin to phenolic monomers: Insights into the effects of solvent, catalyst and atmosphere

Mechanism of synergistic effects and kinetic analysis in bamboo-LDPE waste ex-situ catalytic co-pyrolysis for enhanced aromatic hydrocarbon production via CeZrAl and HZSM-5 dual catalyst

Rationally designed acidic deep eutectic solvent induced catalysis and spontaneous catalyst recycling of Pd-catalyzed ethylene alkoxycarbonylation