Synthesis of a conjugated polymer for sensing ferric/ferrous cations based on dual responses

Yichen Zhang,Hao Zhan,Jiajun Chen,Lijuan Sun,Li‐Juan Fan

DOI: https://doi.org/10.1002/pol.20200231

IF: 3.046

2020-07-12

Journal of Polymer Science

Abstract:A conjugated polymer (PPETE‐RB) with poly[p‐(phenylene ethynylene)‐alt‐(thienylene‐ethynylene)] (PPETE) as the backbone with pendant rhodamine B (RB) groups in the close‐ring spirolactam form was synthesized. With long spacer between backbone and pedant groups as well as long solubilizing side chains, the polymer possesses good solubility in most organic solvents and relatively large molecular weight. The fluorescence of the conjugated polymer in THF exhibited selective dual responses upon adding Fe3+/Fe2+ but negligible response upon other cations. The emission around 481 nm (excited at 360 nm) decreased and that around 571 nm (excited at 520 nm) emerged and increased when increasing the concentration of iron ions. The responses to Fe3+ and Fe2+ are very similar. The limits of detection were found to fall in between 6 μM and 8 μM. The mechanism study showed that the quenching around 481 nm was due to the inner filter effect (IFE) between the Fe3+/Fe2+ and PPETE‐RB; while that enhancement around 571 nm could be attributed to the formation of fluorescent ring‐open structure from nonfluorescent spirolactam of pedant RB group upon Fe3+/Fe2+. Such dual and opposite responses provided more reliable information than single response for sensing applications. A conjugated polymer with poly[p‐(phenylene ethynylene)‐alt‐(thienylene‐ethynylene)] (PPETE) as the backbone and rhodamine B (RB) as the pendant group was synthesized. The obtained PPETE‐RB exhibits dual responses toward Fe3+/Fe2+. The fluorescence is decreased when excited at 360 nm and enhanced when excited at 520 nm, respectively.

polymer science