Abstract:This study reports the formation of Er-doped nanocrystalline cobalt ferrite with the formula CoFe2-x Er x O4 (0.0 ≤ x ≤ 0.10) from nontoxic metal precursors Co(NO3)2·6H2O, Fe(NO3)3·9H2O, and Er(NO3)3·5H2O through an easy and economical sol-gel route in which citric acid is served as the chelating agent. The as-prepared powder was annealed at 700 °C for 3 h in ambient air to get the required spinel structure. The annealed samples were subjected to structural and magnetic characterization. The X-ray diffraction (XRD) data of the samples confirmed the cubic spinel structure formation. The average crystallite size evaluated from XRD data increased from 21 to 34 nm with the substitution of Er due to the larger atomic size of Er3+ than Fe3+. Moreover, the crystallite size obtained from XRD data are well matched with the particle size measured from transmission electron microscopy images. The lattice parameters obtained from XRD data agree well with the values estimated from theoretical cation distribution and Rietveld refinement calculation. The hysteresis curve exhibits the particles are soft ferromagnetic and the coercivity increased from 54.7 to 76.6 kA/m with maximum saturation magnetization, M s = 61 emug-1 for 0.10 Er content. The squareness ratios were found to be less than 0.5, which indicates the single-domain nature of our particles. The blocking temperature measured from field cooled-zero field cooled curves is T B > 350 K for all the samples, which is much higher than the room temperature (300 K). The enhancement of saturation magnetization and coercivity has been explained based on the crystallite size, anisotropy constant, and cation distribution. Thus, the structural and magnetic properties of CoFe2O4 nanoparticles (NPs) can be tuned by Er incorporation and these NPs can be applied in different soft magnetic devices.

Magnetic behavior of nanocrystalline ErCo2

Observation of a Griffiths-like phase in the paramagnetic regime of ErCo_2

Facile Route for the Synthesis of Er Doped Nanoferrites: An Investigation on Structural, Magnetic, and Electrical Properties

Room temperature soft ferromagnetism in the nanocrystalline form of YCo2 - a well-known bulk Pauli paramagnet

Excellent Magnetocaloric Performance in the Carbide Compounds RE2Cr2C3 (RE = Er, Ho, and Dy) and Their Composites

Magnetic and universal magnetocaloric behavior of rare-earth substituted DyFe0.5Cr0.5O3

Magnetic behavior of nanocrystalline LaMn2Ge2

Unusual Magnetic and Transport Properties of Layered Compound ErMn6Sn6

Magnetic behavior of bulk and fine particles of RCr2Si2C (R = La, Ce)compounds: possible magnetic ordering from Cr

Magnetic anomalies in nanocrystalline Ca3CoRhO6, a geometrically frustrated spin-chain compound,

The Magnetic Structures and Transitions of A Potential Multiferroic Orthoferrite Erfeo3

Magnetic behavior of nano crystals of a spin-chain system, Ca3Co2O6: Absence of multiple steps in the low temperature isothermal magnetization

Optical and magnetoelectric coupling studies of ErCrO3

Magnetism of fine particles of Kondo lattices, obtained by high-energy ball-milling

Octahedral tilting and emergence of ferrimagnetism in cobalt-ruthenium based double perovskites

Microstructure, Magnetic, and Magneto-Optical Properties of Chemical Synthesized Co–RE (re=ho, Er, Tm, Yb, Lu) Ferrite Nanocrystalline Films

Magnetic and structural properties of nanocrystalline PrCo$_3$

Sol-Gel Route for the Synthesis of CoFe2- x Er x O4 Nanocrystalline Ferrites and the Investigation of Structural and Magnetic Properties for Magnetic Device Applications

Critical behavior of the cubic ErNi 2 Laves compound nearby the ferro-paramagnetic phase transition

Study of the Structure, Multiferroic, and Magnetic Order of Er0.9La0.1Cr0.8Fe0.2O3

The magnetic structure and spin-reorientation of ErGa