Chemical Substitution Strategies for Tailoring P2- and O3-Type Layered Oxide Cathodes in Sodium-Ion Batteries
Arindam Ghosh,Baskar Senthilkumar,Rashmi Hegde,Subham Ghosh,Penphitcha Amonpattaratkit,Premkumar Senguttuvan
DOI: https://doi.org/10.1149/ma2024-01532772mtgabs
2024-08-09
ECS Meeting Abstracts
Abstract:Among cathodes for sodium-ion batteries (SIBs), layered transition metal oxides Na x MO 2 (M = transition metal) are very promising due to their easy synthesis and high theoretical capacity. 1,2 In this class, Ni/Mn/Fe-based layered oxides are attractive due to the high redox potential of Ni 2+ / Ni 4+ and Jahn Teller inactive centers (Ni 2+ , Fe 3+ ,and Mn 4+ ). 3 However, complex phase transitions, Na + /vacancy ordering and transition-metal (TM) migration degrade their electrochemical performances. 4 To address the issues, a widely studied cathode- P2-type Na 0.67 [Ni 0.33 Mn 0.67 ]O 2 is chosen and Li + is substituted in the TM-layer to tailor a series of high Na-content cathodes. Among them, Na 0.85 [Li 0.14 Ni 0.29 Mn 0.57 ]O 2 cathode with optimal Li-substitution exhibits a reversible capacity of 168 mAh g -1 at 0.1 C rate and good cycling stability (82% retention after 100 cycles). 5 In-situ XRD measurement reveals a complete solid-solution formation and X-ray absorption spectroscopy studies confirm the participation of Ni 4+ /Ni 2+ and Mn 4+ /Mn 3+ redox couples during Na + -extraction/insertion. Lastly, a full Na-ion cell with hard carbon is demonstrated with an energy density of 420 Wh kg -1 . In subsequent work, a Li and Ti co-substitution strategy is applied to design a high-entropy O3-type NaLi x Ni y Fe z Mn 0.5 Ti 0.5-a O 2 cathode. 6 It retains 77% of its initial capacity after 400 cycles at a 2 C rate with a facile O3-P3-OP2-P3-O3 phase transition. The co-substitution strategy uplifts the average voltage of the system, improves the reversibility of the high-voltage OP2 phase, and enhances the Na-ion diffusion rate. A mere 1.32% unit cell volume change and diminishing electrochemical cell resistance over cycling ensure its superior long-term cycling performance. A full cell is fabricated, which holds 62% of its initial capacity even after 1000 cycles at a 0.5 C rate. Therefore, mono- and di-ion substitution strategies hold enormous potential for designing high-performing P2- and O3-type cathode materials for practical SIBs. References T. Hosaka, K. Kubota, A. S. Hameed, and S. Komaba, Chem. Rev. , 120 , 6358–6466 (2020). J. Y. Hwang, S. T. Myung, and Y. K. Sun, Chem. Soc. Rev. , 46 , 3529–3614 (2017). F. Zhang, J. Liao, L. Xu, W. Wu, and X. Wu, ACS Appl. Mater. Interfaces , 13 , 40695–40704 (2021). Z. Lu and J. R. Dahn, J. Electrochem. Soc. , 148 , A1225 (2001). A. Ghosh, B. Senthilkumar, S. Ghosh, P. Amonpattaratkit, and P. Senguttuvan, J. Electrochem. Soc. , 170 , 030538 (2023). A. Ghosh, R. Hegde, and P. Senguttuvan, J. Mater. Chem. A. , submitted(2023).