Facile preparation of silicon/carbon composite with porous architecture for advanced lithium-ion battery anode
Haofeng Shi,Wenyuan Zhang,Donghua Wang,Jiashuai Wang,Chengdeng Wang,Zhihao Xiong,Fu-Rong Chen,Hailiang Dong,Bingshe Xu,Xiaoqin Yan
DOI: https://doi.org/10.1016/j.jelechem.2023.117427
IF: 4.598
2023-04-10
Journal of Electroanalytical Chemistry
Abstract:Silicon is a potential anode material for Li battery due to its high theoretical specific capacity (4200 mAh g −1 ). However, Si is hampered for practical application in Li-battery due to its enormous volume alternation causing instability. Herein, we demonstrated a novel carbon-coated porous structure (/Si-G) synthesized by uniformly wrapping Si into pitch pyrolytic carbon shells and then in-situ removing the sodium chloride template can overcome the bottleneck. It is worth noting that our process for /Si-G also offers a simple route for cost down and mass production of anode material. The /Si-G anodes exhibit an excellent capacity of 1082.7 mAh g −1 at 0.2 C after 200 cycles. Furthermore, it holds a high capacity retention of 81.9 % after 500 cycles at 0.5 C. We found that /Si-G composite only rises about 41% volumetric expansion during 500 operation cycles. This can effectively avoid direct contact between silicon and electrolyte to form a stable solid electrolyte interphase (SEI) film. Especially, practical application of the /Si-G anode is demonstrated in a full cell pairing with LiNi 0.3 Co 0.3 Mn 0.3 O 2 cathode. The full cell presents great cycle retention of 90.1 % at 0.2 C after 100 cycles and a high energy density (446 Wh kg −1 ).
chemistry, analytical,electrochemistry