Enhancement of microstructure and magnetic properties of MgCd ferrite via Sm-Ga ions substitution for microwave devices

Jie Li,Feng Gao,Gang Wang,Yan Yang,Yahui Sun,Haokai Su,Xuening Han,Huaiwu Zhang,Qiang Li
DOI: https://doi.org/10.1016/j.materresbull.2021.111414
IF: 5.6
2021-10-01
Materials Research Bulletin
Abstract:<p>Herein, Sm-Ga ions substituted MgCd ferrite (Mg<sub>0.77</sub>Cd<sub>0.23</sub>Fe<sub>2-2x</sub>Sm<sub>x</sub>Ga<sub>x</sub>O<sub>4</sub>, x = 0.00–0.20) were synthesized via solid state method at low temperature using 2 wt% B<sub>2</sub>O<sub>3</sub>-Bi<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub>-ZnO glass (BBSZ glass) additive. Sm-Ga substitution did not change the spinel phase formation of ferrite. SEM showed that the grain size first increased and then decreased, while the bulk density displayed the opposite trend and the maximum density was 4.646 g/cm<sup>3</sup> at x = 0.10. Owing to Sm-Ga ions substitution, saturation magnetization (<em>M</em><sub>s</sub>) first increased, and then decreased, while the coercivity (<em>H</em><sub>c</sub>) decreased first, and then increased. At x = 0.10, the maximum <em>M</em><sub>s</sub> was 25.33 emu/g, and the minimum <em>H</em><sub>c</sub> was 28.82 Oe. The real part of magnetic permeability reached a maximum (μ' = 56.02 @x = 0.15) and then dropped down. The ferromagnetic resonance linewidth (at 9.56 GHz) was easily influenced by the Sm-Ga ions substitution, with the minimum value of 251.29 Oe at x = 0.10. Hence, the material has potential for microwave devices applications.</p>
materials science, multidisciplinary
What problem does this paper attempt to address?