Ti 3 C 2 MXene-Encapsulated NiFe-LDH Hybrid Anode for High-Performance Lithium-Ion Batteries and Capacitors
Chenyang Li,Dongdong Zhang,Jin Cao,Pengfei Yu,Manunya Okhawilai,Jin Yi,Jiaqian Qin,Xinyu Zhang
DOI: https://doi.org/10.1021/acsaem.1c01171
IF: 6.4
2021-08-01
ACS Applied Energy Materials
Abstract:Layered doubled hydroxides (LDHs) have aroused much attention in energy storage for their exchangeable anions and tunable interlayer spacing. However, poor electrical conductivity and aggregation of flakes cause huge volume changes and reduce accessible active sites, leading to inferior cycle stability and rate performance. Hence, a NiFe-LDH/Ti3C2 MXene hybrid with uniformly distributed NiFe-LDH nanoflakes decorated on MXene nanosheets through a simple hydrothermal reaction is prepared. Due to the synergism between the Ti3C2 MXene conductive frameworks and NiFe-LDH, NiFe-LDH/ Ti3C2 MXene shows a superior electrochemical property for lithium storage. Its reversible capacity is 898.9 mAh g–1 at 0.1 A g–1, and even at 1 A g–1, it still has 726.1 mAh g–1, without capacity reduction in lithium-ion half-cells. In addition, the corresponding lithium-ion capacitor shows a higher energy density and power density, showing huge application prospect in lithium storage.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c01171.Calculations, zeta potential, XRD pattern, N2 adsorption–desorption isotherm curves, SEM images of MAX and MXene, TEM image of MXene, CV and GCD curves of MXene and NiFe-LDH, SEM images and cross-sectional SEM images of electrodes, XPS spectra of the NiFe-LDH/MXene electrode, Nyquist plots, GCD profiles of AC, contrast of lithium storage performance of MXene-based materials, and contrast of energy density and power density (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels