Abstract:The performance of plasma facing material (PFM) in nuclear fusion reactor is dramatically influenced by the synergy between steady heat loading and transient events. The negative and positive thermal stresses induced by a temperature gradient can trigger crack damage and even complete failure. Deep understanding the cracking mechanism is of great significance to optimize structure design and to improve service capability of PFM. Herein we combine the extended finite element method (XFEM) with the cohesive zone method (CZM) in order to unravel the characteristics of inter-granular micro-cracking formation in polycrystalline tungsten (W) by taking account of topological microstructure and external loading condition. From the macro component to the mesoscopic structure, the temperature and stress distributions of W/Cu/CuCrZr monoblock under steady state coupled with cyclic transient event is first numerically investigated and compared with the results from experimental measurement. Then, by using the displacement rate estimated from the heat-energy-variation-induced accumulated plastic strain on the surface of monoblock as a bridge, the inter-granular crack propagation behaviors in the equiaxial grain (EG), gradient grain (GG) and heterogeneous grain (HG) structures of the cross-sectional component and in different surface grain sizes of component are predicted, respectively. It is found that higher heat loading with longer duration time leads to the increment of cumulative plastic strain level so that crack extension rate is accelerated. The GG structure exhibits a remarkable improvement on crack development since the change of inter-granular crack path at the triple point is influenced by the inclined boundary with respect to the loading direction. These results provide valuable insights into the correlation of grain morphology and brittle crack growth, especially focusing on further improvement of PFM.

Micro-pillar compression of proton-irradiated chromium examined using cross-sectional site selection, electron microscopy, and molecular dynamics simulation

Direct quantification of mechanical responses of TiSiN/Ag multilayer coatings through uniaxial compression of micropillars

Plasticity in irradiated FeCrAl nanopillars investigated using discrete dislocation dynamics

Deformation Localisation in Ion-Irradiated FeCr

Emulation of neutron damage with proton irradiation and its effects on microstructure and microchemistry of Zircaloy-4

Modified microstructures in proton irradiated dual phase 308L weldment filler material

Surface growth, inner defects and interface mixing of Cr coating on Zr alloy irradiated by 5 MeV protons at 400°C

Modified deformation behaviour of self-ion irradiated tungsten: A combined nano-indentation, HR-EBSD and crystal plasticity study

Experimental and simulation studies on damage mechanisms of tungsten and molybdenum under compressed plasma flow irradiation

Characterising Ion-Irradiated FeCr: Hardness, Thermal Diffusivity and Lattice Strain

Deformation Behaviour of Ion-Irradiated FeCr: A Nanoindentation Study

A spatially resolved analysis of dislocation loop and nanohardness evolution in proton irradiated Zircaloys

In situ microstructural evolution in face-centered and body-centered cubic complex concentrated solid-solution alloys under heavy ion irradiation

Surface Growth, Inner Defects and Interface Mixing of the Cr Coating on Zr Alloy Irradiated by 5 Mev Protons at 400 °C

Deformation microstructures of non-irradiated and proton irradiated zirconium alloy from nanoindentation creep tests characterised by TEM

In Situ Microstructural Evolution in Fcc and Bcc Complex Concentrated Solid-Solution Alloys Under Heavy Ion Irradiation

Microstructure-based crack formation in tungsten exposed to cyclic transient heating

Deformation behavior during micro-pillar compression in an ordered phase strengthened single crystalline Ni–Cr–Mo micropillars at room temperature

Chromium agglomeration induced by Fe + ion irradiation of Fe-10at%Cr

Size dependence of micro-scale mechanical properties on heavy-ion irradiated tempered-martensitic steel evaluated through nanoindentation and micropillar compression tests

Atom probe tomography characterization of high-dose ion irradiated MA957