High-Yield Two-Dimensional Metal–Organic Framework Derivatives for Wideband Electromagnetic Wave Absorption

Guang Liu,Jiaqi Tu,Chen Wu,Yujie Fu,Chenghao Chu,Zihao Zhu,Xinhua Wang,Mi Yan

DOI: https://doi.org/10.1021/acsami.1c00281

2021-04-23

Abstract:Two-dimensional metal–organic frameworks (2D-MOFs) and their derivatives are promising for catalysis, energy storage, gas separation, etc. due to their unique microstructure and physicochemical properties. Many efforts have been devoted to fabricating 2D-MOFs with challenges remaining in yield and fine control of their thickness and lateral size. Here a versatile strategy has been used involving epitaxial, anisotropic, and confined growth of CoNi-MOF-71 nanosheet arrays, giving rise to excellent quantity and controllability of the 2D-MOFs. Electromagnetic (EM) wave absorption performance has been investigated for the resultant 2D Co/Ni/C derivatives. Compared with the bulk counterpart, significantly increased surface area, conductivity, and shape anisotropy for the 2D derivatives result in enhanced interfacial polarization, conductive loss, and magnetic resonance. As such, optimum EM wave absorption of minimum reflection loss RL_min = −49.8 dB and an ultrawide effective adsorption bandwidth EAB = 7.6 GHz can be achieved at a thickness of 2.6 mm. This work not only sheds light on the performance enhancement for 2D absorbers via synergistic effects of multiple attenuation mechanisms but also provides an effective fabrication route of ultrathin MOFs with high yield and uniform size for extended applications in catalysis, electrochemistry, and optoelectronics fields.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c00281?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c00281</a>.SEM images of CoNi-MOF-71 with different reaction conditions (Figure S1); SEM images CoNi-MOF-71 on different substrates (Figure S2); XRD patterns (Figure S3); cole–cole curves (Figure S4); N2 adsorption–desorption isotherms (Figure S5); Raman spectra (Figure S6); conductivity (Figure S7); eddy current loss coefficient (Figure S8); hysteresis loops (Figure S9); attenuation constants (Figure S10); impedance matching (Figure S11); and comparisons of the electromagnetic wave absorption performance (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c00281/suppl_file/am1c00281_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology