Yb:CALYO shaped crystal fibers: Growth and spectroscopic characterization

Zebin Wang,Jian Liu,Peng Chen,Jie Xu,Jun Guo,Qingsong Song,Yong Wei,Peng Liu,Xiaodan Wang,Xiaodong Xu,Jun Xu,Kheirreddine Lebbou

DOI: https://doi.org/10.1016/j.optmat.2024.115206

IF: 3.754

2024-04-03

Optical Materials

Abstract:Yb:CaYAlO 4 (Yb:CALYO) shaped crystal fibers with different Yb 3+ doping concentration were successfully grown by the micro-pulling-down ( μ -PD) method. The effect of the Yb 3+ concentration on the structure, absorption, emission and lifetime was systematically studied. The strongest absorption peaks of Yb:CALYO crystal fibers are located at 977 nm for σ and π polarization. The micro-photoluminescence indicate that Yb 3+ ions in CALYO single crystal fiber grown by the μ -PD method distributed evenly across a cross-section. The emission cross-section of 5 at.% Yb:CALYO crystal fiber was calculated to be 0.86 × 10 −20 and 1.08 × 10 −20 cm 2 at 983 nm for σ and π polarizations. Benefited from the disordered structrure of CaYAlO 4 crystal, the full width at half maximum (FWHM) at 978 nm was 68.9 nm and 80.9 nm, respectively. The fluorescence lifetime of 2 F 5/2 energy level of Yb:CALYO crystal fibers with concentration of 0.5 at.%, 1 at.%, 2 at.% and 5 at.% was calculated to be 435 μs, 484 μs, 514 μs and 453 μs, respectively. The experimental results show that Yb:CALYO crystal fiber is a potential laser medium for ultrashort laser operation.

materials science, multidisciplinary,optics