Design for a Room Temperature Superconductor

Warren E. Pickett

DOI: https://doi.org/10.48550/arXiv.cond-mat/0603482

2006-05-30

Abstract:The vision of ``room temperature superconductivity'' has appeared intermittently but prominently in the literature since 1964, when W. A. Little and V. L. Ginzburg began working on the `problem of high temperature superconductivity' around the same time. Since that time the prospects for room temperature superconductivity have varied from gloom (around 1980) to glee (the years immediately after the discovery of HTS), to wait-and-see (the current feeling). Recent discoveries have clarified old issues, making it possible to construct the blueprint for a viable room temperature superconductor.

Superconductivity,Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to design a room - temperature superconductor (Room Temperature Superconductor). Since 1964, research on high - temperature superconductivity has gone through different stages from pessimism to optimism and then to wait - and - see. Although a copper - oxide high - temperature superconductor (HTS) with a critical temperature of about 90 K was discovered in 1987 and reached about 130 K in the mid - 1990s, the critical temperature has not been further increased since then. Due to the lack of an effective theoretical explanation for the mechanisms of these high - temperature superconductors, it is impossible to develop new materials with higher critical temperatures through rational design.

In contrast, superconductors based on the phonon mechanism have an accurate microscopic theory, which is applicable to strong - coupling situations, making it possible to design materials with higher critical temperatures. The paper points out that the recent breakthroughs in phonon - mediated superconductivity can be used to provide a rational design scheme to achieve room - temperature superconductors. The core of the paper lies in emphasizing the importance of controlling the coupling strength, rather than simply increasing the absolute value of the coupling strength.

Specifically, the paper explores how to avoid structural instability by controlling the specific momentum of the electron - phonon interaction (i.e., \( \lambda_Q \) or more specifically \( \chi(Q) \)), while maximizing the critical temperature \( T_c \). The author proposes a design scheme to achieve this goal by introducing multiple circular Fermi surfaces in a two - dimensional system and having more phonon branches participate in the coupling. For example, by adding another spherical Fermi surface with a radius of one - eighth of the length of the Γ - K line in the Brillouin zone of MgB_2 at the center of the Brillouin zone, closely - packed Kohn surfaces can be formed within the Brillouin zone, thereby using 90% of the Brillouin zone for strong coupling and significantly increasing \( T_c \).

The paper also discusses the material engineering challenges required to achieve this goal and the theoretical uncertainties, especially when the coupling strength \( \lambda \) is greater than 5, the existing theoretical framework may no longer be applicable. Despite these challenges, the paper still provides a blueprint for designing room - temperature superconductors and points out the directions for future research.