Iron Oxide Nanoneedles Anchored on N-Doped Carbon Nanoarrays as an Electrode for High-Performance Hybrid Supercapacitor
Dongming Cai,Junjie Du,Chenyu Zhu,Qinghe Cao,Longsheng Huang,Jun Wu,Dan Zhou,Qinghua Xia,Tian Chen,Cao Guan,Yongde Xia
DOI: https://doi.org/10.1021/acsaem.0c02238
IF: 6.4
2020-11-16
ACS Applied Energy Materials
Abstract:Iron oxides have been widely recognized in the energy storage field, owing to the high theoretical capacitance, low cost, and environmental friendliness. However, the intrinsic poor electrical conductivities have significantly hindered their practical applications. The rational design of the conductive supports is considered an efficient approach to solve the issues. In this work, a three-dimensional composite structure of the Fe<sub>2</sub>O<sub>3</sub> nanoneedles grown on N-doped porous carbon nanoarrays that are derived from a metal–organic framework on carbon cloth (N-C/CC) is designed. The in situ formed N-C/CC nanoarrays substrate not only exhibits desirable conductivity, but also possesses increased diffusion channels and high mechanical flexibility. Thanks to the unique structure, the Fe<sub>2</sub>O<sub>3</sub>@N-C/CC composite exhibits a high specific capacitance of 183.3 mF cm<sup>–2</sup> at 3 mA cm<sup>–2</sup> and excellent cycling stability with 82.7% capacitance retention after 5000 cycles at 5 mA cm<sup>–2</sup>. Moreover, a quasi-solid-state hybrid supercapacitor is assembled using Fe<sub>2</sub>O<sub>3</sub>@N-C/CC as an anode and /CC as a cathode, and the device delivers a high energy density of 14.1 Wh kg<sup>–1</sup> at a power density of 1500 W kg<sup>–1</sup>. This work demonstrates a different route to develop three-dimensional nanoarray materials for energy storage.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c02238?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c02238</a>.XRD patterns; TEM image of the N-C/CC composite; XPS spectrum and Raman spectra; CV and GCD curves; gravimetric capacitances; SEM images of /CC; electrochemical behavior of /CC; electrochemical performances of aqueous /CC///CC hybrid supercapacitor; Ragone plots at different current densities; and optical photographs of the /CC///CC device tested under different bending angles (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c02238/suppl_file/ae0c02238_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels