Molten Salt Thermal Treatment Synthesis of S-Doped V 2 CT x and Its Performance as a Cathode in Aqueous Zn-Ion Batteries

Weiyan Jiang,Huizhong Shi,Miao Shen,Rui Tang,Zhongfeng Tang,Jian-Qiang Wang

DOI: https://doi.org/10.1021/acsami.2c00201

2022-03-11

Abstract:The lack of suitable cathode materials with a high capacity and good stability is a crucial problem affecting the development of aqueous Zn-ion batteries. Herein, a novel strategy for the modification of V2CTx through molten salt thermal treatment is proposed. In the novel route, S heteroatoms were introduced into V2CTx through a substitution reaction during the dissolution of Li2S in LiCl–KCl molten salts. Then, surface V2O5 was obtained through the in situ electrochemical charging/discharging of the S-doped V2CTx (MS-S-V2CTx) cathode. The assembled Zn/MS-S-V2CTx battery showed a high reversible discharge capacity of 411.3 mAh g–1 at a current density of 0.5 A g–1, an 80% capacitance retention after long cycle stability tests at 10 A g–1 for 3000 cycles, and a high energy density of 375.5 Wh kg–1 in 2M ZnSO4. Density functional theory calculations demonstrate that the improved electrochemical performance of the cathode can be attributed to the introduced S heteroatoms, which considerably reduced the ion diffusion energy barrier for Zn2+ ions and improved the stability of V2O5. This work provides a novel method to produce highly active and stable vanadium-based cathodes for aqueous Zn-ion batteries.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.2c00201.SEM images and EDS analysis, Raman analysis, EIS fitting analysis, Capacitive contribution calculation of CV, XPS analysis of V 2p and Zn 2p, SEM and HRTEM, Cycling performance of commercial V2O5, Table summary of XPS analysis, Table of EIS fitting, and details of the first principles calculation (PDF)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology