W.H.A. Thijssen,D. Marjenburgh,R.H. Bremmer,J.M. van Ruitenbeek
Abstract:We report experimental evidence for atomic chain formation during stretching of atomic-sized contacts for gold and silver, that is strongly enhanced due to oxygen incorporation. While gold has been known for its tendency to form atomic chains, for silver this is only observed in the presence of oxygen. With oxygen the silver chains are as long as those for gold, but the conductance drops with chain length to about 0.1 conductance quantum. A relation is suggested with previous work on surface reconstructions for silver (110) surfaces after chemisorption of oxygen.
What problem does this paper attempt to address?
### Problems the paper attempts to solve
This paper mainly explores the influence of oxygen on the formation of gold (Au) and silver (Ag) atomic chains at the atomic scale. Specifically, the researchers hope to verify the following problems through experiments:
1. **Influence of oxygen on atomic chain formation**: In the presence of oxygen, can the atomic chains of gold and silver be formed more stably, and will the length of the chains increase significantly?
2. **Special behavior of silver atomic chains**: Silver itself is very difficult to form long atomic chains without oxygen. But after the introduction of oxygen, can silver form long atomic chains like gold?
3. **Change in conductivity**: After the introduction of oxygen, how does the conductivity of gold and silver atomic chains change, especially the reason for the low - conductivity phenomenon observed in silver?
4. **Relationship with surface reconstruction**: Will the presence of oxygen lead to the reconstruction of the silver (110) surface, similar to the previous research results, and is this reconstruction related to the formation of atomic chains?
### Main findings
- **Gold atomic chains**: After the introduction of oxygen, the length of the gold atomic chains changes slightly, but on the whole, long chains can still be formed. The introduction of oxygen changes some bond distances of the gold atomic chains, for example, from 2.5 Å to 1.9 Å, which is consistent with theoretical calculations.
- **Silver atomic chains**: Before the introduction of oxygen, silver can only form very short atomic chains (usually only 2 - 3 atoms). However, after the introduction of oxygen, silver can form long chains similar to gold, with the longest reaching more than ten atoms. At the same time, the conductivity of silver decreases significantly, approaching 0.1 conductance quantum \( G_0=\frac{2e^2}{h} \).
- **Conductivity mechanism**: For silver, as the chain length increases, the conductivity decreases rapidly and stabilizes at about 0.1 \( G_0 \). This indicates that the introduction of oxygen changes the electronic structure of the silver atomic chains, resulting in a decrease in conductivity.
- **Surface reconstruction**: The researchers speculate that the oxygen - induced silver (110) surface reconstruction may be related to the enhanced formation of atomic chains. The introduction of oxygen atoms makes the silver surface more likely to be reconstructed, thus promoting the formation of long chains.
### Conclusion
This research reveals the important role of oxygen at the atomic scale, especially in promoting the formation of silver atomic chains. This finding not only helps to understand the physical properties of metal atomic chains, but also provides new ideas for the future design of new nanomaterials.