The noble metals M (M = Pd, Ag, Au) decorated CeO 2 catalysts derived from solution combustion method for efficient low-temperature CO catalytic oxidation: effects of different M loading on catalytic performances
Xiuxiu Cui,Xu Zhang,Yaqi Yang,Ting Chen,Yude Wang
DOI: https://doi.org/10.1088/1361-6528/ac7ed3
IF: 3.5
2022-07-25
Nanotechnology
Abstract:Abstract The noble metal nanoparticles have attracted attention due to their excellent catalytic performance for CO oxidation at low temperatures. M-CeO 2 (M = Pd, Ag, Au) catalysts with different atomic ratios of M/Ce were deposited via solution combustion method. Among them, 3 at% Pd-CeO 2 , 5 at% Ag-CeO 2 and 1 at% Au-CeO 2 catalysts have better catalytic performances. Especially, 5 at% Ag-CeO 2 catalyst shows better low-temperature CO oxidation performance. The catalytic activity for CO oxidation follows the follows the following sequence: 5 at% Ag-CeO 2 (T 50 = 69 °C) > 3 at% Pd-CeO 2 (T 50 = 99 °C) >1 at% Au-CeO 2 (T 50 = 115 °C). Meanwhile, the catalysts are characterized by means of powder x-ray diffraction, scanning electron microscope, transmission electron microscopy, Raman spectroscopy, x-ray photoelectron spectroscopy, Brunauer–Emmett–Teller and H 2 -TPR. The characterization results show that the 5 at% Ag-CeO 2 catalyst has excellent catalytic activity due to the good dispersion of Ag nanoparticles, the specific surface area of the material, and the reduction catalyst between different valence ions. Moreover, the surface of the catalyst enhances the mutual synergy, effectively promotes the generation of oxygen vacancies, and increases the active oxygen content of the catalyst surface. Finally, the catalytic mechanism of M-CeO 2 catalysts is summarized.
materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology