Abstract:Electrochemical production of H2O2 from O-2 via the two-electron reduction reaction (2e-ORR) is a green and safe process that is being heavily investigated. Zeolitic imidazolate frameworks (ZIF) as a subclass of metal-organic frameworks (MOFs) have attracted enormous scientific interests due to their high porosity, excellent mechanical stability, tunable surface properties, and exceptional chemical and thermal stabilities. Herein, a series of pyrolyzed ZIF catalysts (p-ZIF) were synthesized by treating 2-methylimidazole zinc salt (ZIF-8) at high temperatures (900, 950 and 1000 degrees C). During pyrolysis, zinc was vaporized, leaving the metal-free nitrogen-doped porous graphitic carbon materials. The effects of the pyrolysis temperature on the structure and catalytic performance of the p-ZIF catalysts in 2e-ORR were systematically studied. In 2e-ORR in an acidic electrolyte, the p-ZIF catalysts displayed low overpotential, low Tafel slope, and negligible activity loss after 3000 cycles of accelerated durability testing (ADT). In particular, the p-ZIF-950 catalyst possessed the highest H2O2 partial current of 0.185 mA at 0 V vs. RHE, followed by the p-ZIF-900 (0.146 mA) and p-ZIF-1000 (0.135 mA) catalysts. The H2O2 selectivity over the p-ZIF-950 catalyst was also constantly higher than those over the other two p-ZIF catalysts across the potential range investigated and maximized at 89.2%. Highly efficient and durable H2O2 production was demonstrated on the p-ZIF-950 catalyst by the linear accumulation of H2O2 to 522 minol.g(cat)(-1) within 6 h, translating to an H2O2 production rate of 87 mmol.g(cat)(-1).h(-1). The morphology, composition, carbon defect, texture, and surface chemical state were characterized by techniques such as transmission electron microscopy (TEM), elemental analysis, Raman spectroscopy, N-2 physisorption, and X-ray photoelectron spectroscopy (XPS). The p-ZIF catalysts not only nicely carried over the regular rhombic dodecahedral morphology of ZIF-8, but also possessed abundant amount of nitrogen, high specific surface area, and hierarchical pore structure. According to the characterization results, the specific surface area and carbon defect are unlikely the key factors that determine the catalytic performance, while the evolutions of the average pore size and surface content of graphitic N mimicked those of the H2O2 partial current and selectivity on the p-ZIF catalysts. In light of the literature works, the large pore size is proposed to facilitate the in-diffusion of O-2 and out-diffusion of H2O2, while the graphitic N is able to enhance the activation of O-2 and desorption of H2O2, both of which are beneficial to the kinetics of the 2e-ORR reaction.

Hydrogenated Pyridine‐Pyrrole Nitrogen‐Doped Carbon for High‐Efficiency Electrosynthesis of Hydrogen Peroxide in NaCl Electrolyte

Regulating N Species in N‐Doped Carbon Electro‐Catalysts for High‐Efficiency Synthesis of Hydrogen Peroxide in Simulated Seawater

Graphitic N in nitrogen-Doped carbon promotes hydrogen peroxide synthesis from electrocatalytic oxygen reduction

Kinetically Facilitating Two-electron Oxygen Reduction by the Synergy of Multiple Pyrrolic Nitrogen Sites for Ultra-high-yield Electrochemical Hydrogen Peroxide Production

Optimizing Heteroatom Doping for Efficient Hydrogen Peroxide Production via Oxygen Reduction

A Chlorine‐Resistant Self‐Doped Nanocarbon Catalyst for Boosting Hydrogen Peroxide Synthesis in Seawater

Facilitating two-electron oxygen reduction with pyrrolic nitrogen sites for electrochemical hydrogen peroxide production

Pyrolysis-Free Mechanochemical Conversion of Small Organic Molecules into Metal-Free Heteroatom-Doped Mesoporous Carbons for Efficient Electrosynthesis of Hydrogen Peroxide

A Pyridinic Nitrogen-Rich Carbon Paper for Hydrazine Oxidation-Hybrid Seawater Electrolysis Toward Efficient H 2 Generation

NaClO-induced sodium-doped cyano-rich graphitic carbon nitride nanosheets with nitrogen vacancies to boost photocatalytic hydrogen peroxide production

Simultaneously Tuning Band Structure and Oxygen Reduction Pathway toward High‐Efficient Photocatalytic Hydrogen Peroxide Production Using Cyano‐Rich Graphitic Carbon Nitride

Efficient Electrochemical Production of H2O2 on Hollow N-Doped Carbon Nanospheres with Abundant Micropores

A pyridinic nitrogen-rich carbon paper for hydrazine oxidation-hybrid seawater electrolysis toward efficient H2 generation

Nitrogen-doped Carbon Pyrolyzed from ZIF-8 for Electrocatalytic Oxygen Reduction to Hydrogen Peroxide

Highly Efficient Electrosynthesis of H2O2 in Acidic Electrolyte on Metal-Free Heteroatoms Co-Doped Carbon Nanosheets and Simultaneously Promoting Fenton Process

Highly efficient electrosynthesis of H 2 O 2 in acidic electrolyte on metal-free heteroatoms co-doped carbon nanosheets and simultaneously promoting Fenton process

Carboxylated Hexagonal Boron Nitride/Graphene Configuration for Electrosynthesis of High-Concentration Neutral Hydrogen Peroxide

Fragmented Polymetric Carbon Nitride with Rich Defects for Boosting Electrochemical Synthesis of Hydrogen Peroxide in Alkaline and Neutral Media

Electrosynthesis of Hydrogen Peroxide Synergistically Catalyzed by Atomic Co–Nx–C Sites and Oxygen Functional Groups in Noble‐Metal‐Free Electrocatalysts

Unveiling Favorable Microenvironment on Porous Doped Carbon Nanosheets for Superior H2O2 Electrosynthesis in Neutral Media

Enhanced On‐Site Hydrogen Peroxide Electrosynthesis by a Selectively Carboxylated N‐Doped Graphene Catalyst