Stress-thermal Aging Properties of Silicone Rubber Used for the Cable Accessories and Electric-thermal-stress Multiple Fields Coupling Simulation
Li Guochang,Guo Kongying,Zhang Jiahao,Sun Weixin,Zhu Yuanwei,Li Shengtao,WEI Yanhui,,
DOI: https://doi.org/10.7498/aps.73.20231869
IF: 0.906
2024-01-01
Acta Physica Sinica
Abstract:During the long-term operation of a cable, the electrical field, high temperature, and interface stress may cause aging or deterioration of the Silicon Rubber (SIR) insulation of the cable accessories, affecting the combined electrical-thermal-force performance of the accessories, and easily causing discharge faults. In this paper, the electrical-thermal-force properties of silicone rubber for cable accessories under thermal aging and combined force -thermal aging were studied by the method of experiment and simulation. The changes and mechanisms of physical and chemical properties, electrical properties, thermal properties and mechanical properties of silicone rubber were tested and coMPared before and after aging. The changes of electric, thermal and force field of cable accessories caused by the change of SIR material parameters under different aging time and aging form are further simulated. The experimental results show that the crosslinking degree and molecular motion system of SIR will change with the deepening of the aging degree, which will lead to different degrees of changes in the electrical-thermal-force properties of the material. After aging, large agglomeration protrudes and small cavities appear in SIR Section, and the damage is more serious under force-thermal aging. The relative dielectric constant decreases first and then increases with the aging time. The volume resistivity, breakdown strength and flashover voltage all increase first and then decrease. The thermal conductivity increases first and then decreases with the increase of aging time. In addition, with the extension of aging time, the tensile strength and elongation at break decrease gradually. Considering the change of properties after aging, the destruction of SIR materials by force-thermal aging is more serious. The simulation results show that under the two aging modes, the maximum electric field strength at the stress cone root of the cable accessories increases first and then decreases with the increase of time. The electric field strength at the stress cone root of the cable accessories caused by the combination of force-thermal aging changes little, maintaining about 2.2kV/mm. The temperature difference between the inside and outside of the insulation layer is obvious under different aging degrees, and the temperature difference shows a trend of first decreasing and then increasing under both aging modes, and the maximum temperature gradient is 9.15°C. The interface stress at the stress cone root decreased from 0.263MPa to 0.230MPa, a decrease of about 12.5%.This work has guiding significance for the insulation performance evaluation and fault analysis of distribution cable accessories.
physics, multidisciplinary