Abstract:Room-temperature spin-coatable polyoxometalate-based composites are explored for low cost electrochromic capacitive films. A transparent stable K 6 P 2 W 18 O 64 –polyvinyl alcohol (P 2 W 18 –PVA) solution suitable for both rigid and flexible substrates was developed. Electrodeposition of HKUST-1 particles was employed to create pore structures in the film leading to facile ion transportation. The excellent EC performance of P 2 W 18 was fully expressed in this thin film with a thickness of 500 nm. The state-of-the-art record of 95% optical contrast and 1600 stable EC cycles were achieved. An electrochromic energy storage device with a capacity of 7.89 mF cm −2 was realized with MnO 2 as the counter electrode. This strategy for the preparation of highly stable and transparent POM coatings at room temperature is a general and simple solution that is not limited to the preparation of electrochromic films.

Room-temperature spin-coatable polyoxometalate composites for high-contrast, large-area electrochromic capacitive films