Carbonized foams from graphene/phenolic resin composite aerogels for superior electromagnetic wave absorbers

Jinhuan Li,Huanmin Ji,Andong Li,Jiaojiao Zhang,Yi Yan,Linlin Ren,Hongyan Yu
DOI: https://doi.org/10.1016/j.ceramint.2021.06.014
IF: 5.532
2021-09-01
Ceramics International
Abstract:Ultralight graphene/phenolic resin composite aerogels (GPFs) were prepared through the chemical reduction and self-assembly of graphene oxide (GO) in water-soluble phenolic resin, followed by a freeze-drying process; carbonized foams (GPFs(T)) were obtained by the subsequent heat treatment of GPFs at a relatively low temperature (500–700 °C). Although GPFs do not show the qualified reflection loss value of below −10dB, GPFs(T) achieve the greatly enhanced electromagnetic-wave absorbing performance. Specifically, the minimum reflection loss value of GPF1 (500) reaches −22.7 dB at 14.4 GHz with the absorber thickness of 2.0 mm and the effective absorption bandwidth is up to 5.4 GHz (12.4–17.8 GHz). The evolution of electromagnetic-wave absorbing properties from GPFs to GPFs(T) at different temperatures related with different graphene content is explored. GPFs(T) are expected to exhibit high thermal stability and excellent corrosion resistance property, and especially still maintain ultralight nature (e.g the density of GPF1 (500) is only 24.3 mg/cm3). Most importantly, little graphene (as low as 7.5 wt% of GO addition for GPF1(T)) in GPFs(T) guarantees the facile formation of three-dimension (3D) skeleton network and greatly cut downs the carbonization temperature of phenolic resin to achieve the required electromagnetic-wave energy losing ability. The present work provides an effective method to fabricate an ultralight material with exceptional performances including the good electromagnetic-wave absorbing property and the high stability.
materials science, ceramics
What problem does this paper attempt to address?
The paper focuses on the development of a lightweight and high-performance electromagnetic wave absorption material. The research team combined graphene oxide (GO) with water-soluble phenol-formaldehyde resin through chemical reduction and self-assembly to prepare graphene/phenol-formaldehyde resin composite aerogels (GPFs). Subsequently, carbonized foam (GPFs(T)) was obtained through heat treatment at a relatively low temperature (500-700°C). Although the original GPFs did not show ideal reflection loss values (lower than -10dB), the heat-treated GPFs(T) exhibited significantly enhanced electromagnetic wave absorption performance. Specifically, GPF1(500) achieved the lowest reflection loss value of -22.7dB at a thickness of 2.0mm and a frequency of 14.4GHz, with an effective absorption bandwidth of up to 5.4GHz (12.4-17.8GHz). In addition, GPFs(T) is expected to have high thermal stability and excellent corrosion resistance while maintaining its lightweight characteristics, with a density of only 24.3mg/cm³ for GPF1(500). The evolution of electromagnetic wave absorption performance from GPFs to GPFs(T) at different temperatures is also discussed in the paper, which is related to different graphene contents. It is worth noting that a small amount of graphene (as low as 7.5wt% of GO addition) in GPFs(T) ensures the easy formation of a three-dimensional skeleton network while significantly reducing the carbonization temperature of the phenol-formaldehyde resin to achieve the required energy loss capacity for electromagnetic waves. This work provides an effective method to manufacture a lightweight material with excellent electromagnetic wave absorption performance and high stability. In summary, this paper aims to address the limitations of current electromagnetic wave absorption materials in terms of weight, stability, and absorption performance by developing a new lightweight carbonized foam material. This material not only effectively absorbs electromagnetic waves but also exhibits good thermal stability and corrosion resistance, making it suitable for applications in demanding environments such as aviation and navigation.