Influence of Cu content in CeO2 nanoparticles on their antibacterial properties

DOI: https://doi.org/10.1007/s10971-024-06363-3

2024-03-27

Journal of Sol-Gel Science and Technology

Abstract:The CeO 2 nanoparticles (NPs) with different Cu contents were synthesized, and their antibacterial activity was evaluated quantitatively. It was performed for two of the antibiotic-resistant microorganisms that require urgent attention. The materials were synthesized by co-precipitation method in an alkaline medium (pH 9) using a concentration of 20 mM of Cerium nitrate with three different amounts of Copper nitrate (1, 3, and 5 wt%) content. Polyvinylpyrrolidone was used as a dispersing agent, and ammonium hydroxide was used as a precipitant. The obtained NPs were characterized using different techniques to determine the change in properties due to the Cu dopant amount. The X-ray diffraction, electron microscope techniques, and BET method were used to know the particle's structure, morphology, and porosity. From diffraction patterns, all samples showed a cubic CeO 2 structure and no additional peaks belonging to Cu or CuO phases. The crystal size and lattice parameters obtained by Rietveld refinement of XRD patterns decrease slightly according to Cu content, and the d -space of (1 1 1) plane is agreed with the shifting of this intensity toward low angles (2θ). The SEM images show agglomerated particles with sizes between 0.2 and 4 μm, and the TEM images show spherical shape particles with sizes between 7 and 9 nm. The elemental mapping analysis revealed that the Cu atoms are dispersed in the CeO 2 particles. All samples show a specific surface area between 90 and 130 m 2 /g, and there are ink-bottle-shaped mesopores. The quantitative antibacterial test was evaluated according to the ASTM E2149-20 standard procedure. The highest inhibition against Pseudomonas aeruginosa (ATCC 27853) was 72%, with the sample containing 3 wt% Cu. Meanwhile, the antibacterial activity against Staphylococcus aureus (ATCC 25923) was 48% with the highest Cu Content (5 wt%) with 48 μg/mL of NPs. A significant difference was observed between the antibacterial activity of pure CeO 2 and Cu-doped CeO 2 NPs. However, increasing the Cu content in the CeO 2 NPs or increasing the concentration of NPs for the evaluation is necessary to find adequate inhibition for this bacterium.

materials science, ceramics