The Development of a Composite Thin Film Barrier of Tungsten Fe3O4-rGO (FerGO) for the Radiation Shielding of Medical Personnel

Seon-Chil Kim,Jian Hou,Won-Gi Jang,Hong-Sik Byun

DOI: https://doi.org/10.3390/polym16020215

IF: 5

2024-01-13

Polymers

Abstract:Tungsten is the most effective eco-friendly material used for radiation shielding in hospitals. However, despite its commendable density and shielding performance, tungsten faces challenges in miscibility with other materials because of its elevated melting point and strength. In this study, to protect medical personnel against scattered rays, which are indirect X-rays, a lightweight material was prepared by mixing graphite oxide material, considering its thinness and flexibility. Tungsten particles were evenly dispersed in the polymer, and nanofibers were prepared using this blended polymer solution via electrospinning. Concurrently, the process technology was explored to craft a thin film sheet and obtain a lead-like shielding effect. A spinning solution was prepared by mixing Fe3O4-rGO (FerGO) and tungsten. At 60 kVp, 0.1 mm was measured as 0.097 mmPb, at 80 kVp, 0.2 mm was measured as 0.196 mmPb, and at 100 kVp, 0.3 mm was measured as 0.279 mmPb, showing similar shielding performance to lead. As density directly affects the shielding effect, graphene oxide played an important role in increasing the density of the material from 1.941 g/cm3 to 2.302 g/cm3. Thus, this study provides an effective process for producing thin film sheets equivalent to lead.

polymer science

What problem does this paper attempt to address?

The problem this paper attempts to address is the development of a lightweight, flexible, and efficient radiation shielding material to protect medical personnel from scattered X-rays. Although lead-based shielding materials traditionally used are effective, their heavy weight makes them inconvenient for practical applications and poses environmental concerns. Therefore, researchers are attempting to develop a new type of lead-like shielding material by mixing graphene oxide (GO) and tungsten particles and using electrospinning technology to prepare nanofiber sheets. This new material not only has good shielding performance but also features lightness and flexibility, making it more suitable for use in medical environments.