Elimination of cracks in self-assembled photonic band gap crystals

A.A. Chabanov,Y. Jun,D.J. Norris

DOI: https://doi.org/10.1063/1.1737066

2003-12-16

Abstract:Thin colloidal crystals (or synthetic opals) composed of Stober silica spheres typically develop cracks when they are utilized to obtain photonic band gap crystals (or inverted opals). We find that by sintering the silica spheres prior to assembly of the opal these cracks can be avoided. We report the effects of temperature and duration of the heat treatment on 850 nm silica spheres using electron microscopy, thermogravimetry, and light scattering. We also find a large dependence of the refractive index of the silica on the temperature of the heat treatment. This may allow tuning of the refractive index of silica spheres.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the cracking problem that occurs during the preparation of self - assembled photonic band - gap crystals. Specifically, when Stöber silica spheres are used to construct synthetic opals, and silicon infiltration is carried out at high temperatures to form inverted opals, cracks are likely to occur in these crystals. These cracks will seriously affect the optical properties of the materials and limit their applications in photonics.

### Specific background of the problem

1. **Application prospects of photonic band - gap crystals**:
- Photonic band - gap crystals are synthetic materials that can prevent the propagation of electromagnetic waves within a specific frequency range. This property gives them broad application potential in controlling optical signals.
- In order to achieve a photonic band - gap in the optical frequency range, it is necessary to fabricate three - dimensional periodic structures, and these structures must be composed of materials with a high refractive index.

2. **Methods of self - assembled colloidal crystals**:
- Nearly monodisperse micron - sized silica spheres can be self - assembled into colloidal crystals with a face - centered cubic (fcc) lattice structure, that is, synthetic opals.
- These opals can be filled with high - refractive - index materials such as silicon by chemical vapor deposition (CVD) methods, and then the silica spheres can be selectively removed to form inverted opals.

3. **Causes of crack formation**:
- During high - temperature treatment, the silica spheres will shrink, leading to the formation of cracks. These cracks will be transferred to the inverted opals in the subsequent silicon infiltration step, thus affecting their optical properties.

### Solution

The paper proposes a method to avoid cracks by pre - sintering silica spheres:

- **Pre - sintering process**: Before assembling the opals, the silica spheres are sintered as a dry powder at high temperatures and then redispersed.
- **Experimental results**: After sintering treatment at 600°C for 4 hours, the diameter of the spheres shrinks from 850 nm to 792 nm, but no longer shrinks significantly during the high - temperature infiltration process, thus avoiding the formation of cracks.
- **Changes in density and refractive index**: The sintering treatment also leads to an increase in the density of the silica spheres and a change in the refractive index, which may provide a new way to regulate the refractive index of the spheres.

### Conclusion

By pre - sintering silica spheres, the formation of cracks can be effectively avoided during the silicon infiltration process, thereby improving the quality and optical properties of inverted opals. In addition, the study also found that the sintering temperature and solvent history have a significant impact on the refractive index of silica spheres, which provides the possibility for further regulating the optical properties of the spheres.