Ferroelectric and anti-ferroelectric coupling in superlattices of paraelectric perovskites at room temperature

Hans M. Christen,Eliot D. Specht,Sherwood S. Silliman,K. S. Harshavardhan

DOI: https://doi.org/10.1103/PhysRevB.68.020101

2003-06-18

Abstract:Results from dielectric and structural measurements on epitaxial SrTiO$_3$/BaZrO$_3$ superlattices reveal properties that cannot be explained simply in terms of those measured on single films of the constituent materials. For large superlattice periodicities (20/20 and 38/38 structures, i.e. samples in which each SrTiO3 and BaZrO3 layer are 20 or 38 unit cells thick, respectively), the capacitance-voltage curves indicate room-temperature ferroelectricity. For smaller periodicities (7/7 and 15/15), anti-ferroelectric-type behavior is observed, suggesting strong coupling between individual polar layers. This is consistent with recent second-harmonic generation results [A.Q. Jiang et al., J. Appl. Phys. 93, 1180 (2003)] of ordering in SrTiO$_3$/BaTiO$_3$ superlattices. However, both constituents of the structures investigated here are paraelectric. Strain-induced room-temperature ferroelectricity in SrTiO$_3$ and distance-dependent coupling between these layers are proposed as mechanisms leading to the observed behavior.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: in the superlattice structure composed of two ferroelectric materials (SrTiO₃ and BaZrO₃) at room temperature, how to achieve ferroelectric and antiferroelectric behaviors through strain induction. Specifically, the researchers are concerned with:

1. **Coupling of ferroelectricity and antiferroelectricity**: When these perovskite materials, which are usually paraelectric, are stacked in a specific periodicity, can ferroelectric or antiferroelectric characteristics be observed, and are these characteristics different from the behavior of a single thin - film material?

2. **Coupling mechanism depending on layer spacing**: The influence of different layer spacings (i.e., different thicknesses of SrTiO₃ and BaZrO₃ layers) on ferroelectric and antiferroelectric behaviors. Specifically:
- For larger periodic structures (such as 20/20 and 38/38), room - temperature ferroelectricity is observed.
- For smaller periodic structures (such as 7/7 and 15/15), antiferroelectric behavior is observed.

3. **Strain - induction mechanism**: Explore how strain affects the interaction between SrTiO₃ and BaZrO₃ layers, resulting in the appearance of ferroelectric or antiferroelectric behavior. The researchers propose that strain may cause SrTiO₃ to exhibit ferroelectricity at room temperature, and this effect depends on the layer spacing.

### Main conclusions
- **Large periodic structures** (such as 20/20 and 38/38) exhibit ferroelectricity, in which each layer seems to act as an independent ferroelectric or exhibits long - range ferroelectric order.
- **Small periodic structures** (such as 7/7 and 15/15) exhibit antiferroelectricity, which is consistent with long - range electrostatic interaction and domain - formation energy considerations.
- **Strain - induction mechanism**: The researchers believe that strain can induce SrTiO₃ to exhibit ferroelectricity at room temperature, and the required strain amount is much smaller than previously predicted.

Through these studies, the authors hope to reveal the complex influence of strain and layer spacing on the polarization behavior in the superlattice structure, providing a theoretical basis for the further development of new ferroelectric and antiferroelectric materials.