Abstract:Ultrasonic attenuation and phase velocity measurements have been carried out in the ferromagnetic perovskites La_{2/3}Ca_{1/3}MnO_3 and La_{2/3}Sr_{1/3}MnO_3. Data show that the transition at the Curie temperature, T_C, changes from first- to second-order as Sr replaces Ca in the perovskite. The compound with first-order transition shows also another transition at a temperature T* > T_C. We interpret the temperature window T_C < T < T* as a region of coexistence of a phase separated regime of metallic and insulating regions, in the line of recent theoretical proposals.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to experimentally verify the existence of a specific temperature \(T^*\) in some manganate materials, at which unique phenomena related to magnetic phase transitions occur. Specifically, the researchers hope to confirm, through ultrasonic attenuation and phase velocity measurements, that in La\(_{2/3}\)Ca\(_{1/3}\)MnO\(_3\) with a first - order magnetic phase transition, there is another temperature \(T^*\) above the Curie temperature \(T_C\), and within this temperature range, the coexistence of metallic and insulating regions may occur.
### Research Background
Manganites are an important class of functional materials and have attracted much attention because they exhibit the colossal magnetoresistance (CMR) effect. The physical properties of these materials are complex, especially in terms of magnetism and electron transport. Theoretical studies have shown that these materials may have the coexistence of metallic and insulating regions within a certain temperature window, that is, the so - called "phase separation". However, concrete evidence for this phenomenon is still insufficient.
### Main Problems of the Paper
The paper aims to experimentally verify the following hypotheses:
1. **Existence of the Temperature Window**: In La\(_{2/3}\)Ca\(_{1/3}\)MnO\(_3\) with a first - order magnetic phase transition, does there exist a temperature \(T^*\) higher than the Curie temperature \(T_C\), and can special ultrasonic behavior be observed within this temperature range?
2. **Evidence of Phase Separation**: In the temperature range \(T_C < T < T^*\), does the coexistence of metallic and insulating regions really exist?
### Experimental Methods
To verify the above hypotheses, the researchers carried out the following experiments:
- **Ultrasonic Attenuation and Phase Velocity Measurements**: Ultrasonic attenuation and phase velocity measurements were carried out on La\(_{2/3}\)Ca\(_{1/3}\)MnO\(_3\) and La\(_{2/3}\)Sr\(_{1/3}\)MnO\(_3\) using a 5 - MHz transverse wave.
- **Sample Preparation**: High - purity La\(_{2/3}\)Ca\(_{1/3}\)MnO\(_3\) and La\(_{2/3}\)Sr\(_{1/3}\)MnO\(_3\) samples were prepared by the solid - state reaction method, and their oxygen contents were ensured to be close to the stoichiometric ratio.
### Experimental Results
The experimental results show that:
- In La\(_{2/3}\)Ca\(_{1/3}\)MnO\(_3\), the ultrasonic velocity changes abruptly at \(T_C\approx260 \, \text{K}\), indicating the existence of a first - order magnetic phase transition. In addition, obvious anomalies were also observed at \(T^*\approx350 - 360 \, \text{K}\), which is consistent with the theoretically predicted phase separation phenomenon.
- For La\(_{2/3}\)Sr\(_{1/3}\)MnO\(_3\), its ultrasonic velocity only changes at \(T_C\approx370 \, \text{K}\), and it is a second - order magnetic phase transition, and no similar \(T^*\) anomalies were observed.
### Conclusions
The research results support the view proposed by the theory that in La\(_{2/3}\)Ca\(_{1/3}\)MnO\(_3\) with a first - order magnetic phase transition, there indeed exists a temperature window \(T_C < T < T^*\), within which the coexistence of metallic and insulating regions may occur. For La\(_{2/3}\)Sr\(_{1/3}\)MnO\(_3\), its magnetic phase transition is a conventional second - order phase transition, and no similar phenomenon was observed.
This finding is helpful for further understanding the phase separation mechanism in manganate materials and its influence on physical properties.