Nonlinear optical performances of supramolecular 1-(4-Methyl)- piperazinylfullerene[60] - containing polysiloxane

H.I. Elim,J. Ouyang,S.H. Goh,W. Ji

DOI: https://doi.org/10.48550/arXiv.cond-mat/0302463

2003-02-23

Abstract:The nonlinear optical (NLO) properties of 1-(4-Methyl)- piperazinylfullerene[60] (MPF) incorporated with a polysiloxane copolymer denoted as PSI-46 have been studied using nanosecond laser pulses at 532-nm wavelength. The optical limiting performance of MPF itself is poorer than that of its parent C60, while the contribution of PSI-46 attached to the MPF shows marginally improvement from the ratio of MPF/PSI-46(1:2) to MPF/PSI-46(1:6). However, the effect can be neglected to the MPF optical limiting responses. The photoluminescence emission of MPF-containing polymers was slightly improved in comparison with that of MPF. The possible sources for the slightly improvement in the NLO behaviour are discussed.

Materials Science,Chemical Physics,Optics

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the nonlinear optical (NLO) properties of supramolecular polysiloxane materials containing 1-(4 - methyl)-piperazinyl fullerene[60] (MPF). Specifically, the authors focus on the following points:

1. **Optical limiting properties of MPF and its polymer composites**:
- The optical limiting properties of MPF itself and after being compounded with polysiloxane (PSI - 46) were studied.
- The optical limiting responses of MPF/PSI - 46 composites with different ratios (1:2, 1:4, 1:6) at a wavelength of 532 nm were compared.

2. **Photoluminescence (PL) characteristics**:
- The photoluminescence characteristics of MPF, C60 and MPF/PSI - 46 composites were compared.
- The influence of adding different amounts of PSI - 46 on the photoluminescence intensity was analyzed.

3. **Sources of nonlinear optical properties**:
- How the perturbation of the π - conjugated system of MPF by multi - functionalization affects its nonlinear optical behavior was explored.
- The nonlinear absorption characteristics of these materials were further verified through Z - scan experiments.

### Main findings
- **Optical limiting properties**: The optical limiting property of MPF itself is not as good as that of its parent C60. After adding PSI - 46, although there is a slight improvement, it is still generally not as good as C60.
- **Photoluminescence characteristics**: After MPF is compounded with PSI - 46, the photoluminescence intensity is slightly increased, but as the content of PSI - 46 increases, the photoluminescence intensity gradually decreases.
- **Nonlinear optical properties**: The nonlinear optical properties of MPF and its composites are relatively poor, which is mainly attributed to the perturbation of the π - electron system of the C60 cage - like structure by multi - functionalization.

### Conclusion
This study shows that although MPF and its composites with polysiloxane exhibit certain nonlinear optical properties, these properties are generally not as good as those of C60, mainly due to the interference of multi - functionalization on the π - electron system. Future research can further explore how to optimize these materials to improve their nonlinear optical properties.

Regarding formulas, the physical quantities and parameters involved in the paper are as follows:
- Absorbance and molar absorptivity are expressed by the formula:
\[
A=\epsilon\cdot c\cdot l
\]
where \(A\) is absorbance, \(\epsilon\) is molar absorptivity, \(c\) is concentration, and \(l\) is the optical path length.

- The optical limiting threshold is expressed as:
\[
I_{\text{th}}=\frac{E_{\text{th}}}{A}
\]
where \(I_{\text{th}}\) is the optical limiting threshold, \(E_{\text{th}}\) is the energy threshold, and \(A\) is the area.

These formulas are helpful for understanding experimental data and result analysis.