Enlightening the acoustic vibrations of single crystalline gold nanorods by very low-frequency Raman scattering

J. Margueritat,Lucien Saviot,N. Goubet,H. Portalès

Abstract:Gold nanorods (AuNRs) have attracted wide interest in the last decade due to their potential application in many fields. Most of these applications hinge on the shape-dependence of their optical and electronic properties. Besides, crystallinity is likely to play a key role for tailoring properties and functionalities of metal nanoobjects [1]. Single crystalline AuNRs were synthesized using the method described in ref [2]. This procedure includes some modification of the classical seed-mediated method. Using hydroquinone as the reducing agent allowed to synthesize AuNRs with high aspect ratio without appreciable amount of other shapes (see Figure 1a). By varying the synthesis parameters such as the concentration of hydroquinone, seed particles, gold ions and silver nitrate, the AuNRs size and aspect ratio was controlled. The typical dimensions of the AuNRs are of several tens of nanometers in length and their average diameter does not exceed about 8 nm. This work deals with the study by very low-frequency Raman scattering of the acoustic vibrations of AuNRs. The vibrational frequency is sensitive to either the length or to the diameter of the nanorods depending on the nature of the mode. The narrow AuNRs size distribution results therefore in a low dispersion of frequency for each vibrational mode. As a benefit from this low frequency dispersion, the Raman spectra presented in Figure 1b exhibit several narrow bands in the 20-150 GHz frequency range. Calculations were carried out using a homogeneous continuum model taking into account the elastic anisotropy of gold [3] to get a more accurate picture of the studied nanorods. Thanks to the comparison of the measured and calculated frequencies the different bands observed in the Raman spectra are assigned. These results evidence the sensitivity of the low-frequency Raman spectra on the dimensions (length and diameter) and inner crystalline structure of the nanorods.

Materials Science,Physics