Abstract:Electrospun poly(lactic acid) (PLA) nanofibers would seem be poor carriers for drug delivery due totheir hydrophobicity, high crystallinity, weak mechanical strength and burst drug release due to poor compatibility with hydrophilic drugs. Thus, in this work, cellulose nanocrystals (CNC) as reinforcing agents and polyethylene glycol (PEG) as a compatibilizer to increase dispersion of both CNC and tetracycline hydrochloride (TH) in PLA matrix were successfully electrospun. The addition of CNC/PEG reduced fiber diameters, enhanced fiber uniformity, and the water contact angle was decreased from 117.3° for neat PLA to 98.0° for composite nanofibers with 10 wt% CNC/PEG. When drug-loading levels were further increased, the contact angle was decreased from 119.3° to 75.0°, and fiber diameter was decreased from 680 ± 34 nm for neat PLA with 3 wt% THs to 340 ± 17 nm for composite nanofibers with (TH 30%). More interestingly, more than 95.7% of drug contents were delivered within 1032 h, high drug loading efficiencies of composite nanofibers were more than 98%, and long-term sustained release behavior of composite nanofibers was obtained. The composite nanofibers showed good hydrophilicity and biocompatibility with MG-63 cells. Furthermore, compared to neat PLA, a 57.1% improvement in tensile strength and 240% increase in Young’s modulus were achieved for the composite nanofibers with (TH 15%). Additionally, the maximum decomposition temperature (Tmax) of the composite nanofibers with (TH 30%) was improved by 7.7 °C. The composite nanofibers with improved physical and hydrophilic properties, especially long-term drug release, showed good biocompatibility for use as a drug carrier for long-term sustained drug delivery systems and replacing the traditional medical dressings in biomedical applications.

Control of Surface Wrinkles on Shape Memory PLA/PPDO Micro-nanofibers and Their Applications in Drug Release and Anti-scarring

Digital Laser Direct Writing of Internal Stress in Shape Memory Polymer for Anticounterfeiting and 4D Printing.

Heating/Solvent Responsive Shape-Memory Polymers for Implant Biomedical Devices in Minimally Invasive Surgery: Current Status and Challenge.

A medicated shape memory composite of grafting tannin/poly(l-lactide)

CONTROL OF DIMENSIONAL STABILITY AND DEGRADATION RATE IN ELECTROSPUN COMPOSITE SCAFFOLDS COMPOSED OF POLY(D,L-LACTIDE-co-GLYCOLIDE) AND POLY(ε-CAPROLACTONE)

4D printing of PLA/PCL shape memory composites with controllable sequential deformation

A drug-loaded amphiphilic polymer/poly(l-lactide) shape-memory system

Role of Thermal Property and Interface in Shape Memory Polymers

Nano/microstructures of shape memory polymers: from materials to applications

Development of Shape Memory Polymers Micro/nanofiber Membranes in Biomedical Applications

Electrospun PCL-based Polyurethane/ha Microfibers As Drug Carrier of Dexamethasone with Enhanced Biodegradability and Shape Memory Performances

Preparation, shape memory properties and application research of PLA/PCL‐based shape memory polymers doped with Al2O3 and lignin

Programmable Polymers with Shape Memory for Biomedical Applications

Cellulose nanocrystals/polyethylene glycol as bifunctional reinforcing/compatibilizing agents in poly(lactic acid) nanofibers for controlling long-term in vitro drug release

Modulating Mechanical and Shape-Memory Properties while Mitigating Degradation-Induced Inflammation of Polylactides by Pendant Aspirin Incorporation

Recent advances and perspectives of shape memory polymer fibers

Polydopamine-assisted shape memory of polyurethane nanofibers with light-induced tunable responsiveness and improved cell adhesiveness

Poly (lactic acid) electrospun nanofiber membranes: Advanced characterization for biomedical applications with drug loading performance studies

Shape Memory Polymer Fibers: Materials, Structures, and Applications

Water-responsive Shape Memory PLLA Via Incorporating PCL-(PMVS-s-PAA)-PCL-PTMG-PCL-(PMVS-s-PAA)-PCL

Application and Development of Shape Memory Micro/Nano Patterns