Magnetic flux jumps in textured Bi2Sr2CaCu2O(8+d)

A. Nabialek,M. Niewczas,H. Dabkowska,A. Dabkowski,J. P. Castellan,B. D. Gaulin

DOI: https://doi.org/10.1103/PhysRevB.67.024518

2002-09-18

Abstract:Magnetic flux jumps in textured Bi2Sr2CaCu2O(8+d) have been studied by means of magnetization measurements in the temperature range between 1.95 K and Tc, in an external magnetic field up to 9 T. Flux jumps were found in the temperature range 1.95 K - 6 K, with the external magnetic field parallel to the c axis of the investigated sample. The effect of sample history on magnetic flux jumping was studied and it was found to be well accounted for by the available theoretical models. The magnetic field sweep rate strongly influences the flux jumping and this effect was interpreted in terms of the influence of both flux creep and the thermal environment of the sample. Strong flux creep was found in the temperature and magnetic field range where flux jumps occur suggesting a relationship between the two. The heat exchange conditions between the sample and the experimental environment also influence the flux jumping behavior. Both these effects stabilize the sample against flux instabilities, and this stabilizing effect increases with decreasing magnetic field sweep rate. Demagnetizing effects are also shown to have a significant influence on flux jumping.

Superconductivity

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the occurrence conditions and mechanism of the flux - jump phenomenon in Bi₂Sr₂CaCu₂O₈₊ₓ (Bi - 2212) high - temperature superconducting materials. Specifically, through magnetization measurement, the researchers studied the flux - jump phenomenon under the conditions of a temperature range from 1.95 K to Tc (critical temperature) and an external magnetic field up to 9 T. The paper focuses on the following points:

1. **Temperature Dependence of Flux - Jumps**: The occurrence of flux - jumps at different temperatures, especially in the low - temperature range (1.95 K - 6 K), was studied.

2. **Influence of Magnetic Field Scan Rate**: The influence of the magnetic field scan rate on flux - jumps was explored, and it was found that at a higher scan rate, flux - jumps are more frequent.

3. **Influence of Flux Creep**: The influence of flux creep on flux - jumps was analyzed, and it was found that there is a correlation between strong flux creep and flux - jumps.

4. **Influence of Sample History**: The influence of the sample's history (such as previous magnetic field history) on flux - jumps was studied, and it was found that the sample's history has a significant impact on its stability.

5. **Influence of Demagnetization Effect**: The influence of the demagnetization effect on flux - jumps was discussed and was explained as the change in the heat - exchange conditions between the sample and the experimental environment.

Through these studies, the author hopes to better understand the mechanism of flux - jumps, especially the unstable processes in strongly anisotropic superconductors, thereby providing theoretical support and technical guidance for the future applications of high - temperature superconducting materials.