Abstract:Carbon fiber-reinforced polymers (CFRPs) are extensively employed in the aerospace industry due to their excellent properties. Delamination damage occurring at critical locations in CFRPs can seriously reduce the safety of in-service components. The detection and localization of delamination damage using Lamb waves hold significant potential for widespread application in non-destructive testing. However, the choice of damage localization algorithm may produce different delamination damage localization results. This research presented an IRAPID (improved reconstruction algorithm for probabilistic inspection of defects) method derived from the RAPID (reconstruction algorithm for probabilistic inspection of defects) method, aiming to improve the accuracy and reliability of delamination damage localization. Three CFRP curved plates, including a healthy curved plate and two curved plates with delamination damage sizes of Φ20 mm and Φ40 mm, were prepared in the experiment. The detection experiment of the CFRP curved plate using lead zirconate titanate (PZT) as a transducer to excite and receive Lamb waves was conducted, and the influence of excitation signal frequency on the performance of the proposed method was discussed. Under the condition of an excitation signal frequency of 220~320 kHz and a step size of 10 kHz, the accuracy of the delamination damage localization method proposed in this paper was compared with that of existing methods. The experimental results indicate that the IRAPID algorithm exhibits good stability in the localization of delamination damage across the range of frequency variations considered. The localization error of the IRAPID algorithm for delamination damage is significantly lower than that of the DaS (delay-and-sum) algorithm and the RAPID algorithm. As the size of the delamination damage increases, so does the localization error. The accuracy of delamination damage localization is lower in the X-axis direction than in the Y-axis direction. By averaging the localization results across various frequencies, we can mitigate the potential localization errors associated with single-frequency detection to a certain extent. For the localization of delamination damage, Lamb waves at multiple frequencies can be employed for detection, and the detection results at each frequency are averaged to enhance the reliability of localization.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to improve the accuracy and reliability of using Lamb waves for delamination damage location in carbon fiber - reinforced polymer (CFRP) curved panels. Specifically, the paper proposes an improved IRAPID algorithm, aiming to enhance the precision and stability of delamination damage location. In the study, the authors prepared three CFRP curved panel samples, including one healthy curved panel and two curved panels with delamination damages of different sizes (with diameters of 20 mm and 40 mm respectively). In the experiment, lead zirconate titanate (PZT) was used as a transducer to excite and receive Lamb waves, and the influence of the excitation signal frequency on the performance of the proposed method was discussed. In the excitation signal frequency range from 220 kHz to 320 kHz, with a step size of 10 kHz, the accuracy of the delamination damage location method proposed in this paper was compared with that of existing methods. The experimental results show that the IRAPID algorithm exhibits good stability in delamination damage location within the frequency variation range, and its location error is significantly lower than that of the DaS (Delay - and - Sum) algorithm and the RAPID algorithm. As the size of the delamination damage increases, the location error also increases. The precision of delamination damage location in the X - axis direction is lower than that in the Y - axis direction. By averaging the location results at different frequencies, the potential location error of single - frequency detection can be alleviated to a certain extent, thereby improving the reliability of location.

Research on Delamination Damage Localization of Carbon Fiber-Reinforced Polymer Curved Plate Using Lamb Wave

Ultrasonic Full Guided Wavefield for Damage Detection in Curved CFRP Parts

Research on Delamination Damage Quantification Detection of CFRP Bending Plate Based on Lamb Wave Mode Control

An Algorithm Based on Logarithm of Wavenumber Amplitude for Detection of Delamination in Carbon Fiber Composite

Numerical Simulation of Carbon Fiber Reinforced Polymer Composite Delamination Damage Identification Using Lamb Wave and Filtered Back-Projection Method

Delamination Detection in CFRP Laminates Using FOD Sensor

Quantitative non-destructive evaluation of CFRP delamination defect using laser induced chirp-pulsed radar photothermal tomography

A New Laser Ultrasonic Inspection Method for the Detection of Multiple Delamination Defects.

Impact Damage Detection in Patch-Repaired CFRP Laminates Using Nonlinear Lamb Waves

Quantitative Assessment of Delamination in Composites Using Multiple Local-Defect-resonance Modes

Detection and location of damage in fiber reinforced plastics plates by Lamb wave considering material anisotropy

Curvature mode shape-based damage detection in composite laminated plates

Static and dynamic diffuse wave inspection of delaminations in carbon fiber reinforced composites

Quantitative Test of Delamination Defects in CFRP with Surface Interference by Laser Thermography

Air-coupled transducer tilted C-scan for delamination introduced during the manufacturing process in CFRP plates

The Feature Recognition of CFRP Subsurface Defects Using Low-Energy Chirp-Pulsed Radar Thermography

Detecting delamination defects in CFRP plates using nonlinear defect index of air-coupled Lamb waves and adaptively weighted imaging algorithm

Local Wavenumber Method for Delamination Characterization in Composites with Sparse Representation of Lamb Waves.

Delamination inspection in composite laminates with S0 Lamb wave using flexible macro-fiber composite transducers

Rapid Damage Reconstruction Imaging of Composite Plates Using Non-Contact Air-Coupled Lamb Waves

Damage Imaging Post Processing for Delamination Size Assessment of CFRP Aeronautic Structures