Abstract:The notorious zinc dendrite is a severe constraint to the practical application of zinc-based batteries, as the metal tips growing vertically in two dimensions on the surface of the electrodes during cycling and loosely packed sharp edges may pierce through the diaphragm, posing a safety hazard. In this study, physical stress extrusion was used to generate micron- or submicron-sized cracks on zinc metal anodes, which significantly increased the specific surface area of the electrodes and mitigated the local current density of the electrodes. Zinc ion fluxes were significantly dispersed, producing a dense Zn 2 SO 4 (OH) 6 -xH 2 O (ZHS) layer, which differed distinctly from the by-products of the loose upright growth on the surface of Raw Zn (RZn). Additionally, three-dimensional structure of cracked zinc composition allows it to adjust the zinc volume variations during electroplating/stripping, and the abundance of nucleation sites significantly reduces the Zn polarization voltage, resulting in uniform Zn deposition. The average cycle life of the symmetric cell was >400 h at 1 mA cm −2 current density, and nearly 500 cycles at 5 mA cm −2 current density for the asymmetric cell, with an average Coulombic efficiency of 99.3 %. The activation energy substantially declined with the increase in Zn ion flux per unit time (29.615 KJ mol −1 vs. 44.041 KJ mol −1 ), demonstrating efficient desolvation kinetics. Furthermore, the Crack Zn || V 2 O 5 full cell also exhibits outstanding self-discharge performance, with 85 % capacity retention in a 48 h resting charge/discharge testing, superior to the raw zinc foil anode (78.3 %). Herein, a method of creating microcrack configurations on the surface of zinc anodes using stress extrusion was presented, sparing the current density while optimizing the undesirable growth patterns of ZHS by-products.

200 MPa Cold Isostatic Pressing Creates Surface-microcrack Zn Foil for Scalable and Long-life Zinc Anodes

Micro-cracking on the surface of zinc metal improves the cycle performance of aqueous zinc ion batteries

Epitaxial Deposition of Zn (002) for Stable Zinc Metal Anodes

High-pressure deformation exposes zinc (002) crystal planes adapted for high-performance zinc anodes

Long‐cycling Zinc Metal Anodes Enabled by an In Situ Constructed ZnO Coating Layer

Releasing Plating Induced Stress for Highly Reversible Aqueous Zn Metal Anodes

Metallic Particles‐Induced Surface Reconstruction Enabling Highly Durable Zinc Metal Anode

Zinc iso-plating/stripping: Toward a practical Zn powder anode with ultra-long life over 5600 h

Regulated Ion‐Conductive Electrode–Electrolyte Interface by In Situ Gelation for Stable Zinc Metal Anode

Crystal Plane Reconstruction and Thin Protective Coatings Formation for Superior Stable Zn Anodes Cycling 1300 h

Establishing Thermal Infusion Method for Stable Zinc Metal Anodes in Aqueous Zinc‐Ion Batteries

Converting Commercial Zn Foils into Single (002)‐Textured Zn with Millimeter‐Sized Grains for Highly Reversible Aqueous Zinc Batteries

Ultra‐Stable 3D‐Printed Zn Powder‐Based Anode Coated with a Conformal Ion‐Conductive Layer

Construction of ultrastable and high-rate performance zinc anode with three-dimensional porous structure and Schottky contact

A Generic "Engraving in Aprotic Medium" Strategy toward Stabilized Zn Anodes

Regulating "Tip Effect" and Zn2+‐Deposition Kinetics by In Situ Constructing Interphase for Low Voltage Hysteresis and Dendrite‐Free Zn Anode

Interfacial Engineering Regulates Deposition Kinetics of Zinc Metal Anodes

Spraying amorphous carbon coated zinc as powder-based anodes for long-life zinc-ion batteries

An Industrially Applicable Passivation Strategy for Significantly Improving Cyclability of Zinc Metal Anodes in Aqueous Batteries

Galvanic stabilization of Zn Metals for long-life aqueous batteries

Ultraconformal Horizontal Zinc Deposition toward Dendrite‐Free Anode